Recent Progress in Improving Rate Performance of Cellulose-Derived Carbon Materials for Sodium-Ion Batteries

Highlights Enhancing rate performance of cellulose-derived hard carbon anodes from the view of cellulose molecular, crystalline, and aggregation structure is explored. Relationship of storage sodium and rate performance according to theoretical calculation and characterization analysis is illustrated. Cellulose intrinsic microstructure, conversion relationship between the allotropes of cellulose, and the critical influences on cellulose-derived carbon structure are discussed.


Introduction
There are alarming consequences that the burning of fossil fuels and biomass and the gaseous emissions can lead to environmental pollution and global warming [1].Utilizing carbon coupling with other elements, nature creates diverse creatures and provides renewable ways for energy and matter transformation [2].These carbon-based natural resources, such as cellulose, lignin, and so on, have been used as renewable precursors for the preparation of carbon materials.Moreover, due to the short supply of traditional energy materials, alternative energy sources and their environmental availability have garnered significant interest [3].In either energy source, the energy carriers are all based on the smart grid and chemical energy devices.As one type of chemical energy device, batteries with outstanding portability and conversion efficiency are considered superstar devices, that can convert chemical energy to electricity directly [4].
Due to their high safety, wide voltage, and good capacity, secondary batteries such as lithium-ion batteries (LIBs) and sodium-ion batteries (SIBs) have been drawing much attention from scientists [5,6].SIBs as alternative batteries are now being developed owing to the excessive use and the shortage of lithium resources [7].Sodium and lithium are located in the same main group and own similar physiochemical properties, and the distribution of sodium resources is homogeneous and abundant.Unfortunately, the heavier mass and larger radius of sodium ion make the electrochemical performance of SIBs incomparable to that of LIBs.The increasing importance of rate performance for practical applications and commercialization of SIBs is often overlooked, especially the specific capacity at a high rate, that is rate performance.Whereas a higher rate performance is a necessary condition for SIBs to achieve fast-charging devices.Besides, commercial graphite, which is typically an anode of LIBs, cannot be used to storage sodium ions due to several thermodynamic reasons.Obviously, the study of anode materials' rate performance has a far-reaching influence on commercial applications of SIBs.
The progress in discovering appropriate anode materials for SIBs has significantly been accelerated.Carbonaceous materials mainly including graphite, soft carbon, and hard carbon from the view of graphitization degree, have been generally investigated ascribing to their accessibility, non-toxicity, and chemical stability.Graphite possesses a well-structured arrangement [8], wherein carbon layers are composed of sp 2 hybridized carbon atoms.The longitudinal carbon layers are held together by Van der Waals forces, maintaining a layer spacing of 0.335 nm [9].Soft carbon, which is graphitizable non-graphitic carbon at the higher temperature, have more defects, and the inner carbon layer structure is characteristic of short-range ordered and longrange stacked [10].Hard carbon, first mentioned by Dahn's groups in 2000, plays an essential role in studying storage mechanisms of carbon anode materials in SIBs.At present, a good many precursors have been employed for fabricating hard carbons involving polymers like polyacrylonitrile, resinous like epoxy resin and phenolic resin, and biomass materials like roots, stems, and leaves of plants.These kinds of carbons exhibit different electrochemical performances on account of various microstructures [11].When it comes to the precursors of hard carbon, biomass materials with abundant reserves are of major concerns, especially cellulosebased materials [12].
For the past several decades, cellulose-based materials have been used as the typical precursors to produce hard carbon materials owing to their unique network structures, high flexibility and a low coefficient of thermal expansion.Wu and co-authors investigate the relationship between the structural parameters and surface chemistry of cellulosederived carbons, as well as their sodium storage performances [13].It is showed that microcrystalline of cellulosederived carbon exhibits a larger graphite size, leading to the increase of reversible capacity.The detail strengths over other type of carbon materials are as follows.(i) Cellulose is made up of D-glucose units that is an efficient carbon source.When carbonized at high temperature, cellulose forms a carbon-rich skeleton and conductive network.Due to the natural orientation and crystallinity of cellulose, the well-ordered and oriented graphitic structures with a high sp 2 carbon content is formed.(ii) The pyrolysis process of cellulose mainly involves breaking hydrogen bonds at low carbonization temperature, formation of intermediate cellulose, and depolymerization and ring-opening of pyranoid ring at high temperature [14].During the carbonization process, the surface-abundant hydroxy groups can be a great advantage for toughening and combining.The resulting abundant C=O groups of cellulose-derived carbon is beneficial to improve rate performance.(iii) The hierarchical 1 3 structure is constructed through hydrogen bonds and Van der Waals forces of cellulose microfibril.After carbonization, the formed abundant pores and large specific surface area can be utilized as channels for ion diffusion and charge transfer during the battery operation.And (iv) cellulose-based materials generally have a complex composition, which always acts as sacrificial templates during carbonization, that favor increasing the specific surface area and forming hierarchical pore structure [15].
Considering the potential application of hard carbon derived from cellulose and its derivatives in anode materials for SIBs.Many efforts have been devoted to explore structure of cellulose and its derived carbon materials in order to improve reversible capacity and rate performance of carbon anodes [16,17].This review focus on expounding the cellulose intrinsic microstructure and conversion relationship between the allotropes of cellulose, and dissecting the critical influences on cellulose-derived carbon structure.The relationship of storage sodium and rate performance according to the theoretical calculation and characterization analysis is illustrated.It classifies the limitations on improving rate performance in terms of ion diffusion and electronic transfer at cellulose-based carbon materials levels.Furthermore, different strategies for improving rate performance at cellulose materials levels based on above-mentioned limitations are sorted.Finally, it provides a summary of challenges and perspectives for future research in the field of cellulosederived carbon for sodium-ion battery anode.

Cellulose and Cellulose-Derived Carbon Materials 2.1 Physical and Chemical Structures of Cellulose-Based Materials
Cellulose is unique natural polymers, and mainly photosynthesized in higher plants and synthesized by some bacteria, fungi, algae, and unicellular plants and animals [18,19].
It is interesting that the tunicate is the only animal species obtained cellulose in the outer tissues [19].Bacterial cellulose, produced extracellularly by Gram negative bacteria [20], is an important nano-cellulose [21].Hence, cellulose generally exists in higher plant, such as bryophyte, pteridophyte, and seed plant.Although the cell walls of plants are the main source of cellulose, cellulose is surrounded by portion of lignin, hemicellulose, and ash.The cellulose content of plant is distinct, with those in wood (softwood: 40-50%; and hardwood: 45-50%) being lower than those in other plants (60-75%) [18,22].For example, the cellulose content of cotton fiber is from 94 to 95%, and that of kapok fiber is only 64% [23].The specific proportions contents of cellulose from different sources are shown in Table 1.
Clearly, cellulose is composited of repeating cellobiose units linked by β − 1, 4 glycosidic bonds.The glucose units are classified into α-glucose and β-glucose according to the position of hydroxyl group on the six-membered ring (Fig. 1a).Their difference is that the -OH group of α-glucose attaches at C-1 and C-4 position above the ring, whereas that of β-glucose locates at C-1 below the ring.It is well known that the chair formation of glucose is more stable.This is because the C-1 conformation with -OH group locating near ring plane (equatorial hydroxyls) is preferred, and the coordinate perpendicular to ring plane (axial groups) tends to instability [26].The glycoside bond between the glucose units has the property of acetal, is easy to break in the chemical reaction, and the break of the glycoside bond causes degradation of cellulose molecules.
The molecular chain conformation shows various internal rotation heteromorphs.Due to the internal rotation effect, the arrangement of atoms in the molecule structure is constantly changing.In cellulose chains, C-O bond at C-6 has three different conformations, where g and t refer to guache and trans, respectively.For instance, in the gt conformation, C-O bond at C-6 locates in the side of C-O bond at C-5 and at the opposite direction of C-C bond of C5 and C-4.In general, the conformation of natural cellulose is gt conformation, while regenerated cellulose is tg, gt, and gg conformation, as seen in the insertion enlarged view of Fig. 1a.According known as whisker, is formed by a number of long-chain molecules bounding together through intermolecular Van der Waals and hydrogen bonds in parallel or spirals, and its diameter is about 1-3 nm [28].Micro-fibril with the diameter of about 4-8 nm, also named micro-whiskers, formed by several elementary fibrils interacting with intermolecular forces in parallel arrangement [29].Macro-fibril is structural block consisting of multiple micro-fibrils or fibril pairs with radical dimensions of 0.1-0.6 μm [30].Cell is directly formed by macro-fibrils or micro-fibrils stacking with distinct cell border.Finally, a relatively stable cellulose fibril is formed and join together with two aggregated regions, including ordered (crystalline or orientation-aligned region and disordered (amorphous or anisotropic-aligned region [31].It is because of fibrillar structure of cellulose materials, hierarchical porous structure and semi-crystalline structure are formed, and have advantages in anodes of SIBs.
Cellulose is a semi-crystalline material, and the cellulose chains in amorphous region linking the intermolecular hydrogen bonds between at C-2 and C-3, are in a random coil conformation [32].The size of crystal cell is the furthest distance of crystal planes in a microfiber, determines the exposure degree of cellulose chain in the crystalline region.The degree of crystallinity is the ratio of crystal region, depending on its origin, extraction, and pretreatment.Although the density of amorphous region of cellulose is lower than that of the crystalline region, the amorphous region is more likely to react with other molecular groups, which plays an important role in functional design for cellulose-based carbon materials.Meanwhile, the crystalline structure of cellulose has influence on the physicochemical properties and crystalline structure of cellulose-based carbon materials, and provide a perspective for fabricating cellulose-derived carbon anode materials.
There are four different allomorphs of crystalline cellulose named as cellulose I, II, III, and IV, respectively.Their molecular chain structure and repetition distance are almost the same, but the size of crystal cell and stacking of molecular chain are differences.The detailed structure parameters are listed in Table 2.The natural cellulose I crystals are presented in the form of cellulose I α with a triclinic structure and I β with a monoclinic structure [33,34].Cellulose I α accounts for the major component of bacterial or algal cellulose, and tunicates is based on cellulose I β .In higher plants, both cellulose I α and I β are present, locating in the cell wall of primary and secondary layers, respectively.Cellulose I α has a higher crystallinity than I β , while the stability of cellulose I β is stronger than that of I α , that is because cellulose I β is arranged by the reverse parallel molecular chains to form a more stable linear structure.Hence, it is general that cellulose I β is used as the matrix and reinforcing phases to prepare cellulose composites.In order to achieve composite materials with high crystalline and strength, the different crystalline structure of cellulose should be considered [35].Here, let's take flax composed of cellulose I and lyocell derived from cellulose II as exemplars.Although the lyocell fiber with low hemicellulose is significantly weaker strength, it has more effective in accelerating crystallinity and formation of stereo complexed crystallites than flax fibers.Due to its good reinforcing ability and low variability, it is a promising cellulose-based precursors in sustainable application of cellulose-based carbon materials.
The transformation relationship of various cellulose homogeneous polycrystalline is exhibited in Fig. 1b.Based on these, cellulose II is a more favorable thermodynamical structure than cellulose I.Because of weaker stacking interactions, cellulose II possesses a higher reactivity and cellulose III has more accessible channels on crystalline surface.Cellulose IV I was certified by NMR spectra, and the results show that it is lateral disordered of cellulose I β [41].The order direction of cellulose IV I chain is retained but its structure is paracrystalline and disorder in a lateral direction that is quite similar to I β .Liu et al. studied the crystalline structure make effects on degree of hydrolysis of the prepared different crystal cellulose [42].The hydrolysis rates of four different crystalline cellulose allomorphs are in the order of II > III > I > IV.Because cellulose I and IV suffer surface reactions at 478-508 K, while cellulose II and III just swell at that temperature.The hydrolysis reaction occurring in the whole swollen region leads to higher accessibility between the glycosidic bond and the H + catalyst.The various cellulose crystals have different hydroxyl arrangements, which generate molecular chains of diversified polarity.The conversion from parallel chains to antiparallel chains by physicochemical reactions result in the entropy increasing and enthalpy decreasing, whose process is an irreversible reaction.
Apart from the physical structure of cellulose, its chemical composition also plays a pivotal role in determining numerous properties of carbon materials derived from cellulose.The basic molecular format of cellulose is (C 6 H 10 O 5 ) n and the n refers to degree of polymerization (DP), that is the units number of hydro-glucose per polymer [43].The various cellulose materials have different DP value depending on the source of cellulose.The cellulose materials in lab are designed with a lower DP, while natural cellulose such as cotton has a DP ranging from 3000 to 15,000.In general, the DP value of cellulose is closely linked with its strengthen and solubility due to a higher DP value with more tighten molecular structure, the higher strength with longer chain and more difficulty post-treatment.
In addition, three -OH groups play an important part in forming to the highly crystalline regions because of hydrogen bonding actions.It is also determined how difficult to treat cellulose in post-processing.Cellulose is insoluble in most aqueous solvents, but the abundant hydroxyl functional groups on the surface make it good hydrophilic and easy to chemically modify.The cellulose molecule chains groups involved in the chemical reaction include three hydroxyl groups on the glucose group, glycoside bonds to the glucose group, and two hydroxyl groups on the cellulose end. Figure 1c describes the reacting active groups of cellulose molecular chain.
There are many chemical modifications methods about cellulose to prepare cellulose-derived materials via etherification, esterification, oxidation, nucleophilic substitution, and grafting copolymerization [22].The hydroxyl functional groups on cellulose chains positions C 2 , C 3 , and C 6 are the focus of cellulose modification.The primary (OH-C 6 ) and secondary (OH-C 2 and OH-C 3 ) hydroxyl groups have different chemical reaction abilities, whose reactivities different in the sequence of OH-C 6 > OH-C 2 > OH-C 3 [22].For instance, the method of TEMPO selection oxidized cellulose is prior to oxidize OH-C 6 and OH-C 6 is easier to occur substitution reactions than other hydroxyl groups [31].Moreover, the reaction rate of OH-C 6 is ten times faster than that of OH-C 2 and OH-C 3 in the esterification reaction, while the reaction rate of OH-C 2 is twice as fast as that of OH-C 3 .There are two types of terminal-ends in a cellulose chain.The reducing end, in which the C 1 hydroxyl is presented in the form of glycoside hydroxyl group has the property of hemiacetal.C 4 hydroxyl group is free in the non-reducing end, and not involved in any linkage and retains the properties of hydroxyl group [44].Due to the high DP values of most cellulose and the little proportion of terminal-ends, the effect of terminal-ends on the cellulose could be ignored.

Pyrolysis Process and Influence Factors of Cellulose-Based Materials
Standing on the cost-efficient perspective, the cost of cellulose-based materials is less than resin and pitch-based materials.More importantly, the cellulose-based materials derived from natural resources have been employed as renewable precursors for the controlled synthesis of carbon materials, thereby significantly reducing reliance on fossil reserves and promoting sustainable development in human society.Pyrolysis carbonization, hydrothermal carbonization, and microwave-assisted are common strategies to generate cellulose-derived carbon materials.Compare with pyrolysis carbonization, hydrothermal carbonization and microwave-assisted carbonization methods required rigid experimental environment, resulting in higher production and consumed cost.Therefore, pyrolysis is one of the most classical and simple methods towards large-scale converting cellulose to carbon anode materials used in SIBs.Taking account of conductivity requirement for carbon materials used as anodes, the carbonization temperature prefers to be above 1000 °C [13].To better understand of the relationship between cellulose-derived carbon's structure and performance, it is necessary to illustrate the pyrolysis process of cellulose.The mechanisms of cellulose pyrolysis and its derived carbon formation can be seen in Fig. 2. Firstly, cellulose is depolymerized to oligosaccharides, and the glycosidic bonds are cleaved to D-glucopyranose [45].Then, it undergoes intramolecular rearrangement to form levoglucosan, which can form the solid carbon material through various 1 3 pathways, such as dehydration, decarboxylation, aromatization, and intramolecular condensation [46].The pyrolysis process exhibits a distinct characteristic of reduced degree of polymerization.Levoglucosan dominates the by-products of pyrolyzed cellulose I and II, but its concentration decreases with decreasing crystallinity [47].The large amount of hydroxyl of cellulose is very easy to degrade into volatile compounds (CO, CO 2 , H 2 O, and some hydrocarbon, etc.) at low temperatures (≤ 400 °C [48].Meanwhile, these processes usually produce many oxygen-containing heterocyclic rings, which readily transform into aromatic rings through dehydration, decarboxylation, and de-carbonylation reactions as temperature increases, benefitting the formation of cellulose-based derived carbon with interconnected microstructures. The thermogravimetric analysis (TGA), thermogravimetric differentiation (DTG, and differential scanning calorimetry (DSC curves of cellulose are shown in Fig. 3a, and the pyrolysis process of cellulose is consistent with the above conclusions.According to the C 1s XPS in Fig. 3b, removal of O functional groups, including carbonyl (C=O), anhydrides (O-C=O), and ether (C-OR) groups, are the main reaction occurring below 1000 °C [50].In the cellulose pyrolysis process, the changing functional groups and bond types are following water evaporation and volatile fractions at 200-500 °C.The degradation of organic matter with stronger chemical bonds in cellulose appeared at 500 °C or higher temperature [46].Figure 3c illustrates the ternary phase diagram of C/H/O hard carbon derived from bamboo [14].The temperature region of 250-450 °C corresponding conversion with carbon element increasing accord with the cellulose pyrolysis mechanism.In Fig. 3d, it is obvious that the specific surface area (SSA) gradually decreases and distance of graphene planes become closer with the increase in treatment temperature [51].When the carbonization temperature over 1300 °C, SSA keeps a value of 10 cm 3 g −1 .Pyrolysis can cause noticeable changes in both surface functional group and inter/intramolecular bonds of cellulose.
Apart those, cellulose pyrolysis process includes three secondary reactions, that is polycondensation, multiphase interaction, and gaseous phase decomposition.The Fig. 2 The pyrolysis process and reaction path of cellulose at high temperature [49].Adapted with permission [49].Copyright 2015, American Chemical Society depolymerization path of cellulose and cleavage reaction of pyran rings play an important role in the cellulose pyrolysis products during secondary reactions [52,53].These two reactions happen at stage of higher temperature.Depolymerization is process in which cellulose is converted to dehydrated sugars with low degree of polymerization.Levoglucosan as the most important dehydrated sugar, has the highest yield of more than 60%, and a large amount of works focus on that cellulose produces different ways of depolymerization of levoglucosan [54].The process of pyranoid ring opening is an important reaction of cellulose pyrolysis, which involves the formation mechanism of most of the small molecular components of tar except dehydrated sugars [52].Since levoglucosan is the main product of cellulose pyrolysis, and secondary decomposition can produce small molecular products similar to cellulose pyrolysis, many scholars believe that levoglucosan is the primary product of cellulose pyrolysis, while other small molecules of organic matters come from secondary decomposition [55].
The cellulose crystallinity impacts on pyrolysis process of cellulose-based materials [47].Antal et al. proposed the crystalline degree of cellulose would make an effect on carbon solid residues formation.It is because that the cellulose pyrolysis product, levoglucosan, can form the liquid intermediate when the temperature reaches at 300-340 °C of boiling points [56].The liquid intermediate would polycondense into carbon materials during pyrolysis that is critical for the prepared oligo-saccharides products [57].Higher crystallinity degree improves original temperature of cellulose decompose and inhibits intermediate state of cellulose formation, due to good thermal stability caused by hydrogen bonds network [58].However, the substance of non-crystallinity region in intermediate state can also provide an opportunity for dehydration reaction, and boost to generate furans type materials and high carbon residue ratio [58][59][60].Wu et al. discussed pyrolysis behavior of amorphous and crystalline regions of cellulose [59].It is illustrated that the crystalline cellulose with strong hydrogen bonding networks could preserve the sugar ring structure and obtained maximum of ~ 30% on a carbon basis at 250 °C, and that the amorphous cellulose with weak hydrogen bonds allow the liberation of these short glucose chain segments as pyrolysis intermediates, and a maximum of ∼ 3% on a carbon basis at 270 °C.Yu and co-workers used density functional theory (DFT) to investigate the location of hydroxyl groups has a influence on the dehydration of cellulose [61].Hydroxy group of C-2 is prone to dehydration reactions such as pinanol.The intramolecular hydrogen bonds between C 3 -OH and C 5 -OH is more stable compared with other hydrogen bonds.
In term of the crystallization morphology of cellulose, Donohoe et al. studied different cellulose crystallization morphology (cellulose I refers to natural cellulose, cellulose II and III correspond to natural cellulose I treated by ionic liquids and anhydrous ammonia, respectively), which displayed cellulose pyrolysis behaviors and products during pyrolysis process [47].Compared to cellulose-I or II, cellulose-III produces large amount of the same products regardless of its de-crystallization and depolymerization and produces as much or more levoglucosan at all crystallinity (different degree of de-crystallization and depolymerization of cellulose levels.Besides, the different cellulose allomorphs also affect the viscoelastic properties of cellulose during pyrolysis.All in all, cellulose pyrolysis is a complex process.Breaking glycosidic linkage and opening pyran rings happen in different conditions, that would generate various carbon structure and of course occasionally certain byproducts.

Morphology, Crystalline, and Molecular Structures of Cellulose-Derived Carbons
The structure of cellulose-based carbon materials can be controlled by precursors' structure of cellulose, carbonization temperature, heating speed, gas flow, and carbonization methods [62].These various structures such as microspheres, microfibers, microarray hole, nanosheets, nanoshells, and nanosponge are shown in Fig. 4, caused by the diverse cellulose-based materials precursors and unique crystalline linear structure.Cellulose-derived carbon could keep precursors' original microfiber-like morphology at high temperature pyrolysis following slow heating rate, which facilitates ion migration and adsorption [63].For example, cotton-based cellulose with hollow structure easily formed hollow structure carbon.Besides, the nanoshells are synthesized using machine assistance, such as electrostatic spinning with coaxial spinnerets to produce core-shell fibers.
The resulting fiber electrode consists of a cellulose shell and a CMK-3/S(carbon/sulfur) composite core, where the cellulose shell exhibits excellent ion conductivity and can accommodate volumetric expansion effectively [64].Bacterial cellulose can be converted to highly conductive graphitic carbon by high-temperature carbonization, and the obtained bacterial cellulose-derived carbon could perfectly inherit the intrinsic interconnected 3D microfibers structure of precursor [65].
Of note that the proportion of cellulose and lignin in cellulose-based plant affects the carbon structure [49,71].Lignin, as a significant component in plant, contains fewer oxygen atoms and more aromatic rings.After carbonization, it can be easily converted into carbon materials with fewer micropores.According to the proportion of lignin, cellulosederived carbon materials include wood-based [62,72], cotton-based [73], bamboo-based [74], and nanocellulose-based [75,76].Wood-based cellulose-derived carbons are of two types-hardwood and softwood.For hardwood, its pristine structure with more crystalline cellulose scaffolds can be preserved in the carbonization process and only a few carbon nanoparticles can be found in the stable cell wall.Softwood always contains more lignin component (25-30%) that is easy to be hydrolyzed.As a result, the cell wall and plant tissue scaffold of hardwood will break down into small pieces, and then some globular porous carbon nanoparticles form [45]. Besides, more lignin would benefit from preparing stable nonporous carbon materials by direct pyrolysis due to its high aromatic ring contents.The cellulose and hemicellulose containing abundant hydroxyl groups would undergo decomposition and dehydration condensation, which would lead to the formation of plentiful micropores during the pyrolysis [48].Thus, the plant-based cellulose carbon shows both honeycomb and compact structure, ascribed to hemicellulose and other impurity as sacrificial template during pyrolysis.
It is well known that cellulose-based materials precursors with rich oxygen or thermosetting, which tend to be rigid interconnected microstructure and hinder growth of parallel carbon layer.Therefore, the cellulose-based hard carbon has the characteristics of turbulence (turbostratically) and disordered structure.The oxygen groups play a subtle role in the formation of carbon.In general, oxygen mainly exists in the carbon layer, with the functional groups, such as ketone (-C=O), phenol, hydroxyl, and ether (-C-O), and carboxyl groups (-O-C=O-).These oxygen groups could be transferred and degraded to support ion adsorption and diffusion.The mechanism of oxygen groups for sodium ions adsorption is -C=O + Na + + e − = -C=O-Na.When the carbonized temperature exceeds to 1500 °C, the oxygen groups and crosslinking C-C band could induce graphitization of cellulose-based carbon on the condition of enough active energy.Moreover, it is clarified the configuration stability, adsorption capability, and electronic properties of different oxygen groups incorporated the theoretical calculations.Besides, the aggregated structure of cellulose has a powerful influence on structure of cellulose-based carbons.The celluloses extracted from wood, cotton, and bamboo-based plant by chemical pretreatment is cellulose II type, and bacterial cellulose belongs to cellulose I type.As previously Fig. 4 Various structures of cellulose-based carbon materials, including microspheres derived from wood-based cellulose carbon [66], nanosheets derived from cellulose acetate and kraft lignin [67], microfibers derived from bacterial cellulose [63], nanosponge derived from stem pith of helianthus annuus [68], microarray derived from filter paper [69], and nanoshell derived from cellulose [64].Microspheres: adapted with permission [66], Copyright 2016, WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim.Nanosheets: adapted with permission [67], Copyright 2018, American Chemical Society.Microfibers: adapted with permission [63] For the pyrolytic parameters, the carbonization temperature, heating speed, carbonized atmosphere, and flow speed have critical influences on the structure of cellulose-derived carbon materials.Cotton-based cellulose own natural twist and hollow micro-structure.With the carbonization temperature increasing, the micro-structure of cotton occurs collapse and/or rearrangement to form a higher graphitized carbon material.The other cotton-based materials such as catkins [78] and kapok [79], maintain the similar structures after carbonization [80,81].In our previous work, we selected two-step carbonization method to prepare cellulose-based carbon materials [82].Compared with the one-step carbonization of cellulose precursor, the two-step carbonization could achieve the carbon structure with completer and stabler.Moreover, the majority of the carbon microcrystalline structure obtained during the carbonization process is characterized by closed pores resulting from the transformation of open nanopores and ordered carbon crystallites into enclosed voids surrounded by short-range carbon structures (Fig. 5a).
Carbon microcrystalline structure with more graphitic nanodomains can provide effective electrons transfer pathways and stable sodium ions storage behaviors.It is worth noting that the carbon microcrystalline structure, that mainly involves the length L a , thickness L c , stack layers N, interlayer distance d 002 , and graphited degreeI D ∕I G , plays an impor- tant role in regulating structure of cellulose-based carbon materials (Fig. 5b).The feature of an ideal carbon anode is the shorter L a , thinner L c , less stack layer, higher inter- layer distance, and suitable graphited degree I D ∕I G , which favor for upgrading ion diffusion pathways, declining the ion diffusion barrier, and offering the more active sites to ion transport [84,85].In a previous work from our group, cellulosed-based carbon with appropriate microcrystalline structure parameters was prepared by tailoring the structure of precursor through pretreatment [82].The cellulose-based carbon materials show the related structure parameters value of d 002 = 0.39 nm, L a = 0.36 nm, L c = 0.17 nm, and I D ∕I G = 1.81.From crystal face size, the difference in crystal cell structure parameters lies in the carbon layer spacing from 0.33 to 0.37 nm, the thinner thickness and shorter length of the carbon layer and the number of stacked layers.The size and orientation of the graphitic crystallites strongly influences carbon properties and defines the texture, porosity, surface-area, capacitance and electrical conductivity [86].The pore formation and crystal cell size are closely related to pyrolysis process.Some researchers propose that carbon with complete crystallinity, containing graphite-like crystals and serving as sodium ion anode materials, exhibits exceptional electrochemical performance [83].They think that the sodium storage in fully crystalline carbon is solely attributed to reversible intercalation/de-intercalation of Na + within perfectly aligned graphene-like layers, rather than absorption at defects, heteroatoms, and functional groups (Fig. 5f).The proximity of the p-band center of carbon to the adsorption site is crucial for both E a (adsorption energy) and E b (diffusion barrier energies).A weaker (stronger) adsorption and a smaller (larger) diffusion barrier are observed when the p-band center is farther (closer) from the Fermi level [84].The microcrystalline structure of carbon also affects the adsorption and diffusion barriers energy of Na + .Specifically, the distance between carbon layers () has a significant impact on the adsorption energy of Na + ions, while its effect on diffusion barriers energy is weak.Additionally, shorter graphite layer structures with enhanced p-band centers and introduced vacancy defects and bulk oxygen tend to enhance the adsorption of Na + ions.

Relationship of Sodium Storage and Rate Performance in Carbon Anodes
Rate performance is an indicator to evaluate the discharging/charging speed of electrode materials at a given current density that is a key parameter to enhance power and energy density [87].It is well-known that sodium-ion batteries have been limited for large-scale application due to their low power density.At present, the rate capacity of some cellulose-derived carbon materials can be about 300-390 and 236-280 mAh g −1 at the current densities 0.05 and 1 A g −1 [88][89][90][91].In higher current densities of 2-10 A g −1 , the rate capacity is in the range from 130 to 206 mAh g −1 [66,92].This is obviously not adequate for developing high power-energy density of SIBs.
In general, rate performance is characterised with two methods of galvanostatic charging/discharging (GCD measure and semi-empirical equation [93,94].The former measure is often used to obtain the changing capacity with different current density, while the latter method accurately shows the rate dependence of electrode capacity in views of electrode properties, via the feature time linking to charging/discharging process.At present, GCD curves can obviously obtain the decreasing specific capacity with the increasing current density, but it cannot clearly explain for influence factors that limit the rate performance.Several models have been proposed, and tend to think ion diffusion between electrolyte and electrode materials is the main factor limiting rate performance based on ion transfer time constant [95,96].Coleman et al.

Fig. 5
The cellulose-based carbon materials' structure: a microcrystalline morphology [82]; b the structure parameters of a carbon microcrystalline cell; c-e the values of L a , d 002 , and L c calculated by characterization methods in our previous work [82]; f the sodium storage mechanism for complete crystalline carbon [83].a and c-e, adapted with permission [82], Copyright 2022, Elsevier Limited.f adapted with permission [83].
Copyright 2022, Elsevier Limited 1 3 [93] proposed the semi-empirical equation, which fit the relationship of capacity and rate data to assess the rate performance.The semi-empirical equation is as follows: In Eq. ( 1), fitting rate and Q/M data can get three parameters (Q M , τ, n) to quantify rate performance, where Q/M is the measured specific capacity (mA h g −1 , generally normalized to active mass), and can substitute Q/A (area capacity) and Q/V (volumetric capacity).While R is the , where Q M is the low-rate specific capacity and τ is the characteristic time associated with charging/discharging data [93,97].Taking a series of bacterial cellulose-derived carbons as an example to illustrate rate performance.Figure 6a, b shows that the electrochemical performance of cellulosederived carbon anode materials obtained by liquid (SBC-1300) and vapor phase (T-BC-1300) modified cellulose precursors [82].The GCD curves of Fig. 6a exhibit the discharging capacity of four prepared samples.T-SBC-1300, that suffer from liquid and vapor phase treatment, indicates higher capacity (420.6 mAh g −1 at 30 mA g −1 ) than that of other BC-based carbons.The rate performance of these carbons can be seen in Fig. 6b that all display good capacity reversibility when the current density back to 50 mA g −1 .According to above-mentioned semi-empirical equation, the fitting curves are shown in Fig. 6c, that describe the relationship between electrode capacity and rate; and it is dependent on the diffusion time of ions in the electrode material.It is well-known that the total capacity decreases with current density increasing.That is because the current density of electrons is more than that of ions in the interface between the electrolyte and electrode, resulting the polarization and metallic plating is more likely to happen at high current density.
The total capacity of anode is sum of plateau capacity and slope capacity.In the typical discharging/charging curve, at 0.1 V position is a cut-off point to divide slope (above 0.1 V) and plateau (below 0.1 V) regions.There also is different plateau voltage, like 0.25 V [98] and 1.2 V [63], because some hard carbons have unique microstructure or heteroatomic doping.Based on the "card house" model proposed by Dahn, different views on the specific sodium storage mechanism of hard carbon have emerged one after another.It mainly contains "insertion-filling" [99], "adsorption-insertion" [100], "adsorption-insertion-filling" [101], "adsorption-filling-insertion-deposition" [102], "extended adsorption-insertion" [9], and "adsorption-filling" [50] models.Therefore, three distinct sodium storage mechanisms observed in hard carbons: intercalation within graphite layers, adsorption at surface edges and defects, and filling of nanopores.These various statements about storage sodium mechanisms are closely related to the hard carbon's precursors.
All these different mechanisms can be subsumed under two broad categories, including the diffusion-controlled intercalation behavior and surface induced capacitive behavior.At present, it is widely acknowledged that hard carbon consists of randomly oriented graphitic layers and a wide range sized voids and pores, forming a turbostratic structure with large interlayer distance [81,103].Based on the structural features, the storage sodium ions behavior includes Na + insertion/extraction from microcrystalline graphite interlayer, Na + adsorption on edge defect, vacancy and surface function groups, and Na + filling pore structure with nanoclusters.Na + ions are adsorbed onto defect/edge sites and partial filled in micropore in the slope region above 0.1 V.The storage sodium behaviors of adsorption at edge and defects supply pathways for sodium mobility and sodium storage active sites.The enhancing surface-controlled capacitive is a viable strategy for improving rate capability of carbon-based materials.In the plateau region below 0.1 V, Na + ions intercalate into the graphitic layers while additional adsorption takes place near the cutoff potential within the micropores.Meanwhile, sodium cluster arises from the high concentration of Na + ions present in these micropores below 0.1 V.
The quantitative analysis of capacity-behavior and diffusion control behaviors is proposed by Conway [104][105][106].According to the equations of I(v) = av b and , the proportion of capacitive and diffu- sive capacity in anode materials at specific current density is calculated [63,76].It is noted that the range of b value determines the storage behavior of sodium ions.Here, the scale of b value is 0.5-1; when b value is 0.5 means that storage sodium behavior is dominated by diffusion control, when b value is 1 means that it shows capacitive storage sodium behavior, while when b value is between 0.5 and 1 means that two above-mentioned behaviors are co-existence.The values of k 1 and k 2 can be calculated by fitting the plots of i(v) v 1∕2 as a function of v 1∕2 .Besides, k 1 v 1∕2 and k 2 v represent diffusion-controlled intercalation behavior and surface induced capacitive behavior at a fixed voltage.Based on these, the rate performance of Bacterial cellulosederived hard carbon is characterized in our previous studies, as shown in Fig. 6d-g.
Given that cellulose-derived carbon materials based the storage sodium mechanism illustrated above, the favorable structure of cellulose-derived carbon includes short range order and suitable carbon layers distance (0.36-0.40 nm) [107,108], internal micropores (or voids between graphitic domains) [109,110].Figure 6h exhibits a big difference in rate capacity caused by different microstructure parameters of carbons derived from various precursors.The connection between scan rates and normalized capacity may diagnose ion-diffusion process whether rate-limiting step [89].Wang et al. [111] used hemp haulm to synthesize three-dimensional free-standing hard carbon, that exhibits the plateau capacity of 140 mAh g −1 through reconstructing carbon surface at high current charging/ discharging process in favor of sodium ions insertion.In addition, Chen et al. developed hard carbon via starches 1 3 fermentation and carbonization, where plateau capacity is contributed to pore filling [112].Zhou et al. [113] prepared porous carbon derived from rosewood with rich closed pore and proposed the plateau capacity of 189 mAh g −1 based pore filling mechanism.
In our opinions, the plateau capacity is very important, even a limiting factor for improving the rate performance of SIBs [84].In particular, the charging capacity of halfcell at below 0.1 V vs. Na/Na + is considered a standard to certify practical capacity of anode.The two types of higher plateau (0.4-0.7 V) and lower plateau (below 0.1 V) are divided [114].The higher voltage capacity corresponding to oxygen function groups of carbon surface boost the capacitive storage, and lower voltage capacity through sodium ions insertion.A higher charge potential would reduce work voltage window of practical full cell.The increasing reversible capacity below 1.0 V vs. Na/Na + is an effective method to increase rate capacity.In general, the microstructure parameters of hard carbon, such as d 002 , L a , L c , defect degree (I D /I G , and porous distribution have much influence on the plateau capacity of anode materials [115][116][117].
Recently, developing fast-charging batteries is a hotpoint, to reduce charging time consuming by accelerating reaction kinetics in batteries [118].The achieving of high-power and fast-charging need anode materials with excellent rate performance.Heubner et al. [119] used experimental procedure based on current controlled EIS with varying amplitudes to verify in terms of applicability of the Butlere-Volmer equation for charge transfer kinetics.The Butlere-Volmer equation describes the relationship between the activation overpotential and the resulting current density.The equation is as follows [119]: where j 0 is the exchange current density and η ct is the activation overpotential, and z, F, R, and T are the valance, Faraday's constant, the universal gas constant, and the absolute temperature.The anodic charge transfer coefficient α a is set to 0.5 most of the time in battery modeling and simulation assuming α a + α c = 1.
Both the charge transport and ion diffusion are limited in terms of quantity and quality at high current densities, in which the quantity refers to the transport/diffusion total number of charge and ions and the quality represents the transport rate and diffusion accessible path/space of ion and charge [120].Generally speaking, electron transfer need higher order and ion diffusion need more space [121].There are so much strategies on improving the charge transport and ion diffusion by modifying microstructure [122][123][124], introducing defects and vacancy, designing pore structure, regulating graphite degree, and optimized precursors [125,126] at cellulose-based carbon materials level.Unfortunately, a serious of measures are accompanied by low initial coulombic efficiency (ICE [5] and reducing plateau capacity [127].Therefore, it is important to find the equilibrium relationship between ion diffusion and electron transfer in order to enhance rate performance of SIBs.

Limitations of Cellulose-Derived Carbon Materials at Rate Performance Level
Rate performance for SIBs is actually closely related to power density.Nowadays, the popularization of high-power equipment and portable equipment is becoming more and more important for the rate performance.Currently, the cellulose-based hard carbon materials are a good candidate for SIBs anode, but its rate is really unsatisfied the requirements of higher power density of SIBs.Table 3 illustrates the electrochemical performance of cellulose-based carbon materials as SIBs anode.Good electrode materials need high reversible storage capacity and rapid ions and electrons transport [114,128].However, natural properties of cellulose-based materials bring some roadblocks in carbonization process.To our knowledge, the electronic conductivity and sodium ion diffusion coefficient of cellulose-based hard carbon are ~ 10 2 S cm −1 [129] and ~ 10 -9 -10 -13 cm 2 s −1 [84], respectively, that are much smaller than that of alloy anode materials (such as Na 3 Sb and Na 15 Sn 4 ) of ~ 10 4 S cm −1 [130].
The key parameters for high-rate capacity of cellulosebased materials are the electron conductivity and ion diffusion.The former is the number of sp 3 hybrid orbitals between two carbon atoms, and the latter is caused by disorder structure of cellulose with various directions [139].To some extent, SIBs can be polarized at high current rate, resulting the potential safety and low kinetic problems.The poor rate capacity of hard carbon in half-cells is attributed to the low-potential plateau behavior of hard carbon and the polarized Na counter electrode at high rates [140].Defects, nanopores, and microcrystals are the three crucial structural parameters determining the performance of sodium storage in cellulose-derived carbon.The interaction between the defective carbon layer and sodium ions significantly influences the charge storage state of sodium ions in cellulose-derived carbon, meanwhile the size distribution of nanopores affects the characteristics of clusters formed by sodium within these pores.The order structure of cellulose-based materials provides more electron percolation paths in the bulk volume and reduces near surface resistance [141].Therefore, meticulous attention should be given to the design of cellulose-based materials and cellulose-derived carbon on building robust charge transport network and optimizing valid ion transport paths. 1 3

Electronic Conductivity of Cellulose-Derived Carbon Materials
Electronic conductivity is a behavior happening in internal transportation of electrode materials and interface between current collector and electrode.The electronic conductivity closely relates to the charge-transfer resistance, such as specific resistance of electrode, contact resistance between electrode and electrolyte, ion-diffusion resistance in the bulk electrolyte [120].The charge transfer during electrochemical intercalation is commonly understood as the movement of ions across the interface between the material and electrolyte.It is often assumed that the activation energy associated with this step determines the rate capability of batteries based on intercalation [142].Generally speaking, electrode resistance is smaller, and electric conductivity is larger.Cellulose-based carbon exhibits lower electronic conductivity due to its disorder structure.The enhanced electric conductivity is an important approach to boost the Na + storage reversibility and rate-performance by accelerating the charge transfer kinetics.Besides, the interfacial ion conduction would be facilitated in the reduced space-charge regions, and the less accumulated electrons at interfacial anode could decrease the SEI-induced interfacial resistance.
In addition, electrical conductivity depends on both the concentration and mobility of charge carriers.According to energy band theory, electrons of valence band across the forbidden band and enter to conduction band.Here, the relationship between carrier concentration and electronic conductivity follows the below equation [143][144][145]: where σ is the electronic conductivity, n is the carrier concentration, and μ e is the carrier mobility.|e| is charge absolute value.
There are holes and free electrons in anode materials, and σ could be further described as shown in the following equation [144]: where n i and p i are the concentrations of electrons and holes, respectively, μ e and μ h represent the mobility of the electrons and the holes, respectively.Based on Eq. ( 4), the increased n i and p i are beneficial to enhance the conductivity of anode materials.For example, doping heteroatoms could offer more electrons or vacancy and strength electronic local structure in the manner of introducing non-intrinsic carriers, (3) = n|e| e (4) = n i e e + p i e h that benefit for increasing electron conductivity of carbon materials [63,66,80].Of course, adding conductivity agent or coating could also boost electrons diffusion of electrode materials by introduced intrinsic carriers to achieve improved conductivity.
It is well-known that cellulose is not inherently electrically conductive.Therefore, the cellulose-based carbon materials only have a good electric property by carbonization at higher temperature.With the temperature increasing, the proportion of C-C of sp 2 and sp 3 hybrid orbitals can change, and form the unregular and disorder microcrystalline carbon structure.That determines on the electric property of cellulose-derived carbon structure [13].Here, sp 2 orbitals carbon generally represents honeycomb graphene layer, and sp 3 orbitals carbon refers defect areas.Yu's group [146] prepared cellulose-based aerogels via pyrolysis at 1300 °C that exhibits good electrical conductivity of 0.35 S cm −1 .In comparison to commercial graphite with a conductivity of 6 × 10 4 S m −1 , it is evident that the cellulose-derived carbon obtained through direct carbonization exhibits certain limitations.
In general, the graphitization degree increases and the conductivity becomes better with an enhancement of carbonized temperature.However, the improvement of graphitization degree results in more order carbon microcrystalline structure, and less interlayer distance, and defects, which is unfavorable to the improving plateau capacity.Besides, both inter-and intra-molecular strong hydrogen bonds of the cellulose chain bring some difficulties for further processing of cellulose.On the one hand, the inter-and intra-molecular strong hydrogen bonding limited the carbon layer rearrangement, ascribing to molecular chain cannot extend.A significant number of crystalline regions occurs directly crosslinking to form carbon microcrystalline structure, to some extent limiting optimization of crystal cell structure parameters during carbonized process.On the other hand, intermolecular chains have strong hydrogen bonds lead to the harder modification and more complex preparation process.It is difficult to adjust its crystal structure, thus affecting the optimization of carbon microcrystals, further to limit the improving for conductivity.Bacterial cellulose, methyl cellulose, hydroxypropyl cellulose and carboxymethyl cellulose were in situ polymerized with aniline and obtained the four conductive cellulose fabrics.The electrical conductivity value of the four fabrics were 1.990 × 10 -2 , 2.840 × 10 -2 , 2.080 × 10 -2 , and 0.962 × 10 -2 S (2024) 16: 148 148 Page 18 of 46 https://doi.org/10.1007/s40820-024-01351-2© The authors cm −1 , respectively [147].Therefore, cellulose type has influence on the electrical conductivity of cellulose.

Ion Diffusivity of Cellulose-Derived Carbon Materials
The ion diffusion in anode materials as an essential parameter to estimate rate performance and power density of metal-ion batteries, and expressed as diffusion coefficient (D i .The ions diffusion behavior of carbon electrode is evaluated by performing coulometric titration measurement, electrochemical impedance spectra (EIS), cyclic voltammetry (CV), and galvanostatic intermittent titration technique (GITT).Both EIS and GITT methods can obtain the ion diffusion in electrode materials, and the diffusion behaviors can be observed from the spectrum at low-frequency region of EIS.However, all these calculation methods are suitable to qualitative analysis due to uncertainty electrode area.Note that the diffusion coefficient calculated by above methods is apparent coefficient.It actually represents that the ion diffusion pathway between the solid-state anode materials and liquid electrolyte.
In here, ion diffusion can be calculated by coulometric titration technique [148] and GITT method [132] as follows: In Eq. ( 5), d E /d δ is the slope of the coulometric titration curve, V M is the molar volume of the sample, I 0 is the constant current, and F is Faraday's constant, and dE/dt 1/2 is the short-time instantaneous voltage change slope.In Eq. ( 6), τ is for the pulse duration, m B (g and M B are the active mass and molar mass of carbon, V M is the molar volume, and S (cm 2 ) is the active area of the electrodes.The parameters of ∆E S and ∆E τ are the potential changes at τ and relaxation stages per GITT step.It should be guaranteed the time τ of the current flux is small compared to L 2 /D i .Just as importantly, the CV and EIS [149,150] are used by some researchers, and the detailed process is calculated as shown follow: (5) In Eqs. ( 7) and ( 8), i p is the current, n is the number of transferred electrons, A is the electrode area, C is the metal ion concentration, D i is the diffusion coefficient, v is the scan rate of cyclic voltammetry, σ is the exchange coefficient for a completely irreversible reaction σ = 0.5, and n α is the number of reaction electrons in the rate-controlling step (n α = n when approximating the treatment).In Eqs.(9)(10)(11), j 0 refers exchange current density, the σ and w are the Warburg coefficient and angular frequency, A is the electrode surface area, n is transferred electrons numbers, F is the Faraday constant, C is the concentration of Na + , T is the absolute temperature, and R is the gas constant.According to Eq. ( 10), it could be seen that the lower the value of σ (Warburg impedance coefficient), the higher diffusion coefficient.The value of σ is calculated by the linear fitting slope [17].
The lattices of cellulose-derived carbon materials change with different synthesis methods that affects the migrating ions.The understanding and optimizing ion mobility for the development of advanced and efficient battery materials is very important [151].A shortened ion diffusion path facilitates the enhanced mobility of ions within both the electrode and electrolyte, thereby resulting in an elevated ion diffusion coefficient.Through considering factors such as ion diffusion coefficients, capacity, and ion diffusion lengths, the rate performance of carbon materials would be improved.The rate of ion diffusion is highly dependent on the diffusion coefficient (D i and the length (λ) of materials, which can be mathematically expressed using Einstein's formula [120]: where τ is the diffusion time; λ is the diffusion length, which is up to the geometric size of the active material; D i is the diffusion coefficient depending on the architecture of the active material, which is increased by designing the most appropriate architecture providing spacious diffusion pathways.Undoubtedly, the diffusion kinetics (the migration rate, τ) relies on the crucial factors of ionic diffusivity and diffusion length.Hence, it is imperative to enhance ion diffusivity (D i in both bulk and surface domains while simultaneously reducing diffusion length (λ).In this regard, nanoscale (9) materials have gained significant popularity owing to their small particle size, which effectively narrows down the diffusion length (λ) and enhances charge transfer efficiency [152].
According the paths of ions transportation, pore structure is the most important parameters should be taken account for improving rate performance of SIBs.Generally, cellulosebased materials with three-dimensional network and rich oxygen groups are beneficial to produce cellulose-derived carbon materials with abundant porous structure.However, the interconnected intermediate state forms due to the breaking of intermolecular chains bonds, resulting the porosity decreases in the carbonized process.Besides, the cellulosebased carbon materials are easier to form stacking carbon sheets due to hydrogen bonds and Van der Waals' force of cellulose chains.This structure is unfavorable for enlarging the distance of carbon layers, inhibiting sodium ion diffusion kinetics in the carbon derived from cellulose-based materials.
Moreover, there are types of pores occurring in the carbon materials, such as closed pore, open pore, micropore, mesopore, and so on.These pores have a different effect on improving ions diffusion.For examples, open pores are conducive to stabilize carbon structure at discharging/charging process.The rich accessible closed pores exhibit good diffusion ability [153] that is helpful to improve plateau capacity by expanding pores filling.In addition, the ultra-micropore is deemed to hinder contact between carbon surface and liquid electrolyte, which can achieve high rate performance [114].Our group has done a lot of work on controlling pore structure of cellulose-based carbon materials for SIBs anode [76,82,133].However, the high crosslinking density of cellulose makes the degradation and rearrangement of carbon framework more difficulties, even at the higher carbonized temperature [153].Especially for the carbon derived from natural cellulose materials with high crystalline degree, it has not enough defects and vacancy sites to support ion diffusion in carbon interlayers.
A whole electrode includes current collector, active materials, conductive agents and binders, and its ion transport is influenced by the electrode architectures, such as porosity, conductivity, tortuosity, and spatial heterogeneity [154].The limited rate capability is often attributed to solid-state diffusion limitations.Commercial electrode typically possess a thickness ranging from 50 to 100 μm and a areal mass loading about 10 mg cm −2 [155].The sluggish kinetics of ion transport, resulting from the enhanced active materials loading, hinder ions penetrate into the active sites within the electrode material matrix.The compaction density influences the electrochemical reaction induced by electrolyte diffusion.Solid-state electrolytes are highly anticipated in alkali metal batteries due to their exceptional ionic conductivity, wide electrochemical stability window, low electrical conductivity, and remarkable chemical stability.However, one major challenge lies in achieving superior interfacial contact between the solid-state electrolytes and solid electrodes because affected electrics/ions transport [156].The electrode's stability must be considered to improve the battery's rate performance, as exposure to air leads to reactions between water, oxygen, and carbon dioxide with the electrode components [157].In the past decades, nanoengineering has been extensively employed to reduce the solidstate diffusion length and enable both rate performance and capacity utilization.

Solid Electrolyte Interphase on Cellulose-Derived Carbon Materials
Both ions diffusion and charge transport are passing through interface between cathode/anode and electrolyte.Thus, the profound impact of "external" factor-solid electrolyte interphase (SEI on the functionality of electrodes attracts widely attention) [158][159][160].Due to the solvation ability of polar solvents in electrolytes, the cations readily coordinate with the solvent, leading to the formation of diverse solvation configurations.Upon reaching the electrode surface, these solvated cations undergo de-solvation and decompose their solvation shells to generate a SEI layer.The transfer impedance of Na + at the electrode/electrolyte interface is reduced by maintaining a low ion-electrolyte bonding energy during the insertion/extraction process of Na + [161].The surface free energy of carbon materials is determined by factors including the distribution of carbon atoms in inner layers and surface edges, polar functional groups, heteroatom doping, and defects on surfaces and pores of carbon materials.These factors collectively limit the stability, robustness, and integrity of the SEI layer formed on carbon electrodes while also restricting improvements in rate performance for SIBs.Because of the violent reaction of alkali metals with water, a sodium-based battery would require an organicliquid Na + electrolyte [162].Electrolyte of a sodium-ion battery typically comprise carbonates based and ethers based, corresponding to varying types of sodium salts.The electrolyte ions act as charge carriers exist in form of solvation structure, as is depicted in Fig. 7a.Additionally, the plating of metallic sodium from an organic-liquid electrolyte during charging leads to the formation of anode whiskers (dendrites).These dendrites can grow across a thin separator towards the positive electrode, causing internal short-circuits and the flammable electrolyte igniting.To address the safety concern, significant efforts have been dedicated to in-situ formation of a stable SEI film and construction of artificial SEI layers on electrode surfaces, serving as an effective strategy for mitigating dendrite formation or impeding dendrite penetration [156,163].
From electrode perspective, the fundamental requirements including chemical compatibility, wettability, morphology evolution of electrode have important influences on the SEI stability, as are illustrated in Fig. 7b, c.The cellulosebased carbon exhibits a network structure with functional groups and defects, which remains intact even after high temperature treatment.The abundant groups and defects on the surface accelerates electrolyte decomposition and easily leads to excessive activity, which makes to form a thicker and more heterogeneous SEI [168].In our group studies, we Fig. 7 a The solvation structure; b requirement of high ionic conductivity and fast ion transportation between the electrode and electrolytes; c requirements for the electrode surface [160]; d different SEI components in different electrolytes [164]; e inferior electrolyte-philic electrode materials; f superior electrolyte-philic electrode materials [165]; g Na + ions number density inside nanopores [166]; h alkali-metal storage states on the carbon layer due to the M-M (mental-mental) and M-C (mental-carbon) interactions [167].a-c Adapted with permissioned [160], Copyright 2022, the Royal Society of Chemistry.d Adapted with permissioned [164], Copyright 2022, the Royal Society of Chemistry.e-f Adapted with permissioned [165], Copyright 2023, the Royal Society of Chemistry.g Adapted with permissioned [166], The Royal Society of Chemistry.h Adapted with permissioned [167], Copyright 2020, Elsevier B.V 1 3 conducted a comprehensive analysis of the impact of interface properties on energy storage behavior, with a specific focus on investigating the electrochemical reaction occurring at the interface between electrodes and electrolytes [165,169,170].Although the cellulose precursor is easily modifiable due to its abundant hydroxy groups, the type and contents of oxygen functional groups still a limit for optimizing electrochemical performance of SIBs [171].Precisely introducing oxygen functional groups into cellulose or cellulose-derived carbon structure to form more stable SEI layer remains a challenge.
It is reported that oxygen function groups introduced into carbon crystalline structure would boost sodium storage kinetics behaviors that relates to SEI composition dominated inorganic or organic components.As shown in Fig. 7d, the constituents of SEI typically consist of organic and inorganic compounds, which is generated through the decomposition of polar solvents and sodium salts [172,173], respectively.Obviously, the formation of an unstable and thick SEI leads to the successive loss of limited charge carriers, resulting in a rapid drop-off in capacity and limiting the achievable rate capacity. Figure 7e, f illustrates the inferior electrolytephilic and superior electrolyte-philic electrode materials from interfacial faradaic reaction to bulk faradaic reaction in metal ion batteries.Optimal compatibility between the electrolyte and electrode is essential in preventing undesired side reactions and rapid capacity decay, while superior electrolyte wettability can mitigate battery reaction polarization.
Cellulose-based carbon are composed of small, oriented graphene fragments, which randomly form a network of interconnected micropores and mesopores through the numerous voids created by their haphazard arrangement [174].Considering that storage sodium mechanism of Na + filling in the pore of carbon anode, Na + concentration after entering into nanopore effect carbon surface charge density due to pore size, as shown in Fig. 7g.Na + can easily enter inner pore with the pore surface density increasing [166].Besides, the natural and charged pore produces various influence due to surface charge density except uniform pore and slit pore.However, the deposition sodium mental in the pore is considered an unfavorable situation in the charging/discharging process.In Heather's work, ex-situ 23 Na solid-state NMR was chosen to investigate the formed metallic sodium clusters.It is found that Na + ions are absorbed at carbon edge and pore surface, forming quasi-metallic sodium in nanopore with increasing of discharging depth [115].The size of Na metallic clusters increase with nanopore diameter increase, resulting a declined capacity of SIBs and safety problem caused by sodium dendrite in the long-time cycling [175].
Designing a cellulose-derived carbon anode materials with an appropriate pore structure can effectively prevent the deposition of metal sodium inside.Sodium metal exhibits distinctive lattice energy and de-solvation energy and would dissolves in some concentration electrolyte.Specially, the atomic interactions, in Fig. 7h, that is, the interplay of metal-metal (M-M) and metal-carbon (M-C, between the carbon layers and Na ions decide their varying charge storage states in hard carbon anodes [176].When the dominant interaction is M-C, alkali-metal atoms tend to exist as metal ions with charges close to 1. Conversely, alkali-metal atoms tend to form quasi-metallic clusters with charges between 0 and 1 when the dominant interaction is M-M.The quasi-metallic clusters are notably different from bulk metal formed by metal plating, varying significantly in charge states, sizes, and morphology.The various parameters have a profound impact on the plateau capacity of hard carbon anodes in the low potential region, which indirectly limits the improvement of rate capacity in SIBs.

Strategies for Improving Rate Performance from Perspective of Cellulose-based Materials
According to the limited factors that influence on rate performance mentioned in Sect.4, the strategies for improving rate performance of cellulose-based carbon materials are summarized at the cellulose materials level.Our group discussed the inherent limitations in cellulose-based materials, which encompass impurities within components, a singular chemical structure, uncontrolled crystalline texture, and irregular porous architecture, and further provided an opinion that a pretreatment strategy is necessary to fabricate cellulose-derived materials [177].Here, two strategies including building robust charge transport network and optimizing valid ion transport pathways, have been developed to obtain the higher rate capacity of cellulose-derived carbon materials at cellulose materials level.Figure 8

Building Robust Charge Transport Network
A good cellulose-derived carbon electrode requires a wellestablished charge transport network to provide excellent electronic conductivity.The cellulose's natural structural feature is an abundant intertwining fiber network that can provide a rich electronic transport channel for cellulosebased anodes materials.Besides, the exceptional crystallinity and mechanical strength of cellulose can establish a stable electrode framework favoring to enhance electronic transfer.For instance, the rate capacity and reversible capacity of cellulose-based carbon are superior to that of lignin-based carbon [13], because single molecule-oriented microcrystalline of cellulose promotes the radial growth of graphite microcrystalline, which facilitates the rearrangement of aromatic rings.The rate performance is determined by the number of electronic carriers, thus doping heteroatoms, combining with conductive materials, and polymerizing in Fig. 8 The strategies of improving rate capacity of cellulose-derived carbon materials at cellulose materials level.Optimizing valid ion transport paths strategies on the above line are doping in cellulose precursors [178,179], combining in cellulose precursors [180], and polymerizing in cellulose precursors [76]; building robust charge transport network strategies on the below line are introducing defects and groups [181], improving the crystalline structure [73,89], and regulating porous structure [182].Doping: Adapted with permission [178,179]

Pre-doping in Cellulose Precursors
Some methods about heteroatom doping into carbon materials or precursors are various, whose methods include insitu doping in cellulose-based precursors [66,183] and doping in cellulose-derived carbons at carbonization process [63], i.e., pre-doping and doping, respectively.There are a large amount of atoms that have been reported to be used as dopant, such as N (nitrogen), S (sulfur), P (phosphorous), B (boron), and F (fluorine, and so on, which could change microstructure and enhance physicochemical properties of obtained carbon materials [63,66,75,80].Although many researchers have reported on the relationship between doped structure and electrochemical performance, there is currently no evidence detailing how does heteroatom doping influence structure and performance when work as electrode materials.Among these heteroatoms, N atom is more likely to form chemical bonds with atoms in the adjacent vicinity.Generally, N atom is always from NH 3 , polyacrylonitrile (PAN), polypyrrole (PPy), polyaniline (PANI, and so on.N bond are divided into pyrrolic N, pyridinic N, and quaternary N according to bonding environments [184].Surface conjugate structure and electron distribution density of carbon material is changed after doping N, leading to increased electrical conductivity and wettability.In Fig. 9a, the N-doped carbon nanofibers obtained by pyrolyzed bacterial cellulose in-situ growth amorphous Fe 2 O 3 , which shows good rate performance, and a rate capability of 408 and 183 mAh g −1 at 0.1 A g −1 and 3 A g −1 [185].High N content of 10% offers more active site for Na + , facilitating electronic transport, as can be seen in Fig. 9b, c.The rate performance exhibits smaller capacity fluctuation, suggesting N-doping forming pyridinic nitrogen adsorption ion by its outermost shell free electrons boost storage sodium, and pyridinic nitrogen would be created defects to increase conductivity of carbon materials.Apart from N-doping, N/S-doping presents an alternative approach to enhance conductivity and electrochemical performance.Via a "green" and low-cost route Xu et al. prepared hierarchical N/S co-doped carbon microspheres (NSC-SP) by pyrolyzing the cellulose/PANI composite microspheres [66].As shown in Fig. 9d, the microsphere morphology increase adhesion between collector current and active materials.Meanwhile, the nanosized interconnected nano-walls could provide not only connected pathways for electrons but reduced distance for Na + ion diffusion.It is not ignored that the charge accumulation at the composite interface between the two phases of composite may hinder the efficient charge transfer.Figure 9e describes the carbon structures of common graphite, undoped hard carbon, and N/S co-doped hard carbon with different interlayer distances and their influences on the Na-storage capabilities.The conclusion can be drawn that N/S co-doping expands the distance between carbon interlayers and elevates the Fermi level, resulting in electron-rich carbon materials.This enhancement of electronic conductivity facilitates rapid electron transport, thereby contributing to superior sodium storage performance and excellent rate capability [66].
S-doping is a proper choose to develop high-rate capacity carbon anode materials and promote the electronegativity as well as electrochemical activity [80].Introducing S atoms into sp 2 carbon framework leads to the formation of various sulfur bonding species, including thiol, thiophene (aromatic sulfur), thioether/sulfides (aliphatic sulfur), sulfoxide, sulfone and sulfonic acid [178], as illustrated in Fig. 10a.According to Jin's research, bacterial cellulose was pyrolyzed at 800 °C and then mixed with sulfur powder at 500 °C in an Ar 2 atmosphere for S-doping.The synthesis process is illustrated in Fig. 10b [63].The content of S is up to 15 wt%, enough covalent bonds -C-S-C-) to be linked with carbon nanofibers.Sulfur-dope carbon nanofibers (shorten as S-CNF obey capacitive-like storage sodium and reveal high-rate capability of 257 mAh g −1 at 8 A g −1 , attributed to the surface adsorption of Na + in the nanovoids, defects, and S-doping covalent bonds.Figure 10c is the diffusion routes for Na + transfer, and the enlarger interlayer distance has a lower diffusion barrier and better Na + mobility.From the density of states (DOS) maps in Fig. 10d, the bandgap of the S-doped carbon material is reduced compared to that of the undoped configuration due to defect formation, thereby enhancing the electrical conductivity and demonstrating exceptional rate capability [63].
Compare to N and S, the atom radius of P is larger and donates electron to form chemical bonding in carbons [187].P doping could improve the charge transfer between sodium and carbon atom bonded with P, strengthening the adsorption of sodium ions.Long bond length of P-C results in a pyramidal-like bonding configuration, as the P atom is pushed away from the carbon plane.This distortion is due to the sp 3 configuration often exhibited by P atoms and leads to an open edge morphology [178,188].The introduction of phosphorus doping into carbon initially results in the presence of unstable reduced states, which are gradually oxidized by oxygen groups and humidity to form various oxidized P-containing functional groups [189], as illustrated in Fig. 10e.Tao et al. used H 3 PO 4 , hydrazine hydrate, and urea to synthesis N, P dual-doped hollow carbon fibers/graphitic carbon nitride (huCP/g-C 3 N 4 ) using the common filter paper as a precursor [186].In Fig. 10f, huCP/g-C 3 N 4 exhibits outstanding rate performance of 93 mAh g −1 at 5 A g −1 , and the reversible capacity still keep 280 mAh g −1 when the current density is back to 0.1 A g −1 .As can be shown in Fig. 10g, the formed conductive network of g-C 3 N 4 nanoparticles and N, P dual-doped hollow carbon fiber facilitate the electronic transport and ionic diffusion.
The Boron atom exhibits a higher affinity for accepting electrons from Na atoms compared to P atom, resulting in enhanced ionic interaction and binding energy.This is attributed to the incorporation of B into C lattice, leading to substitution of certain C sites by B which acts as an electron acceptor [190].When B is doped on the carbon layer edge, binding energy of heteroatom and Na + would be increased due to B bond with oxygen [191].B-doped carbon anode promotes the diffusion dynamics of Na + between microcrystalline interlayers, hence facilitating a diffusion-controlled Na + insertion process [192].Fluorine is an electronegativity atom and endow it ability to reduce repulsion for insertion and extraction of Na + , that is, energy barrier of Na + insertion is impaired, and more storage site for Na + binding [193].Similar to B-doping, single atom doped of F-based cellulose precursors carbon has no literature published.1 3

Combining High-Conductive Materials into Cellulose Precursors
Cellulose-based materials can maintain their natural structure after pyrolysis and provide anchoring sites to immobilize active nanoparticles, but their electron conductivity is poor.To address the issue of weakened charge transfer pathways in cellulose-derived carbon materials, a common strategy is to combing with a high conductive material.The internal electronic structure and composition of carbon electrode materials can determine the reaction rate and transfer process, and the electrochemical properties can be changed by adjusting the structure of electrode materials [181].
Liu and co-workers prepared bacterial cellulose @ polypyrrole composites materials (C-BC@PPy) with a porous carbon network structure and short-range ordered carbon [194].The anode demonstrates a high capacity of 248 mAh g −1 after 100 cycles at 0.05 A g −1 , and maintains a Fig. 10 a Types of sulfur groups in carbon matrix [178].S-doping [63]: b preparation of S-doped carbon nanofibers; c the diffusion path of Na + ; and d the undoped and S-doped carbon density of states.e Types of phosphonic groups in the carbon matrix [178].Double atoms doping [186]: f rate performance of huCP/g-C 3 N 4 as anode for SIBs; and g electron transfer and Na + diffusion of huCP/g-C 3 N 4 electrode.a Adapted with permission [178], Copyright 2020, Elsevier B.V. b-e Adapted with permission [63] Copyright 2018, The Royal Society of Chemistry.f, g Adapted with permission [186] Copyright 2017, Elsevier Limited capacity retention of 176 mAh g −1 even after 2000 cycles at 0.5 A g −1 .Tang et al. [180] synthesized nanocomposite with BC nanofiber-supported PANI using in-situ polymerization, and its electronic conductivity is up to 5.1 S cm −1 .In Shi and co-workers' work, they used graphene as an initiator accelerated carbonized cellulose nanofiber (CNFs) with the help of a microwave.The sodium in the carbonaceous materials, introduced from the carbonization of CNFs containing sodium-ion carboxyl, offers favorable spaces for sodiation/ de-sodiation, and still maintains in cellulose-based carbon matrix suffering heat treatment to provide an active site for Na + transportation and intercalation [135].The microwaving graphene oxide/cellulose nanofiber (MrGO-CNF chemical variations are shown in Fig. 11a, where the reduction of graphene oxide (GO) occurs upon the removal of oxygencontaining functional groups during the 300 °C treatment, while simultaneous removal of partial functional groups takes place in CNFs.The first discharging capacity is 558 mAh g −1 , including the capacities of 226 mAh g −1 from the sloping region and 332 mAh g −1 from plateau region.Besides, MrGO-CNF displays great rate performance of 100 mAh g −1 at 3.2 A g −1 and return to 0.02 A g −1 with 320 mAh g −1 discharging capacity, as can be seen in Fig. 11b.
Combining the cellulose precursors with mental organic framework (MOFs) establish a continuous charge transfer mechanism represents a promising approach for constructing a robust network facilitating charge transport.As Fig. 11c, Li and colleagues synthesized a unique three-dimensional porous electrode material by utilizing an in-situ growth method to decorate bacterial cellulose nanofiber networks with Co 3 O 4 nanoparticles, followed by controlled pyrolysis to obtain Co 3 O 4 @N-CNFs [184].The Co 3 O 4 @N-CNFs exhibited a porous morphology as revealed by scanning electron microscopy (SEM) in Fig. 11d, which was attributed to the nanofiber network structure derived from bacterial cellulose.Within this carbon framework, uniformly interconnected Co 3 O 4 nanoparticles were embedded.This unique porous architecture not only provided ample space for accommodating the Co 3 O 4 particles but also facilitated efficient electron transport.Thus, the Co 3 O 4 @N-CNFs exhibit a rate capability with current densities of 3,200 mA g −1 and an average discharging capacity of 205 mAh g −1 .
The incorporation of metal nanoparticles into cellulosebased composite materials has the potential to enhance the performance of carbon materials derived from cellulose.The cellulose-based materials can be effectively utilized in conjunction with various metal and metal oxide counterparts, for example, Co 3 O 4 , Fe 3 O 4 , CuO, and ZnO [184,185,196,197].Through the coordination of copper ions (Cu 2+ ) with one-dimensional cellulose nanofibrils, Hu et al. discovered that the opening of molecular channels within the typically ion-insulating cellulose allows for rapid transport of ions with high ion conductivity (1.5 × 10 -3 in the direction of molecular chains).This enables Cu 2+ ions to move along the polymer chains, resulting in elevated conductivities [196].Furthermore, the localized carbon structure can be readily modulated by introducing M-N x -C coordination (M, N, and C denoted as metal, nitrogen, and carbon atoms, respectively) to achieve fast bulk Na + transportation [198].Lu et al. have successfully synthesized a hard carbon material by incorporating zinc single atoms at the atomic level.This incorporation allows for modulation of both the bulk and surface structure of the hard carbon.The resulting Zn-N 4 -C architecture exhibits catalytic activity in rapidly decomposing NaPF 6 and facilitating fast SEI interfacial Na + storage kinetics.Additionally, it induces a local electric field within the graphitic domains, which provides an advantageous Coulombic force to accelerate bulk Na + storage kinetics by reducing diffusion barriers [108].Furthermore, this work suggests potential strategies for further enhancing the rate performance of hard carbon materials and extending these improvements to cellulose-derived carbons.
Soft carbon has a higher degree of order, better conductivity, smaller layer spacing, and excellent rate capacity [199].The structure combination hard and soft carbon enables to form a novel carbonaceous material, thereby optimizing the electrochemical performance as anode materials [200].Qiu et al. prepared soft carbon coated on hard carbon surface through with tissue soaking in pitch and then high temperature carbonization [195].Figure 11e exhibited capacity maintain ratio of carbon paper at different current density.The carbon paper (HC-P-1200) shows good rate capacity due to the long-range-ordered soft carbon terminates the graphene edges of hard carbon.It leads to that reduces SEI formation and the subsequent consumption of sodium-related active substances.Besides, the change trend of plateau and slope capacity display that soft hard coating is a strategy for improve plateau capacity as shown in Fig. 11f.As FTIR of Fig. 11g shows that the soft carbon obtained by direct heat treatment at the same temperature has fewer oxygen-containing functional groups than cellulose-based hard carbon.The slope capacity is reduced by less oxygen-containing defects inhibiting the irreversible capture of sodium ions.Hence, integrating hard carbon with soft carbon represents an effective strategy for obtaining carbon materials with high capacity and excellent rate performance.

Introducing Macromolecules into Cellulose Precursors Via In-Situ Polymerization
In 2021, a conductive cellulose nanofiber with graphitized carbon shell extracted directly at lower temperature and pressure via confined chemical transitions method is firstly proposed [201].The conductive carbon nanofibers exhibit outstanding electron conductivity of 1.099 S cm −1 .This safe and simple method provide a guideline for cellulose-based high conductivity carbon preparation, but its production process enhances technical costs and yield lower.In this regard, a few researchers studied polymerizations in cellulose precursors for introducing macromolecular components to not only increase carbon yield, but well control cellulosederived carbon structure via in-situ polymerization, emulsion polymerization, and heat treatment.Several polymer macromolecules, such phenolic resin, epoxy resin, glucose, and dopamine are also employed as hard carbon precursors due to their convenient morphology design and absence of impurities.Because of strong hydrogen bonding, cellulose-based materials are easy to aggregate.Therefore, introducing macromolecules into cellulose precursors via in-situ polymerization can prevent the aggregating and achieve preferred structure of hard carbon, thereby enhancing electrochemical performance [202].
Cellulose was selected by Dobashi et al. to regulate the discontinuity of the polymer carbon network after grinding the powder during electrode preparation, BC-PAN composite materials were synthesized through the incorporation of BC gel into PAN monomer (Fig. 12a).The composites followed by carbonization at 1000 °C to yield cellulose-derived carbon with a continuous porous network structure [203].Cellulose-derived carbon structures exhibit a cross-linked BC network structure within a PAN porous framework, featuring microscale layered and nanoscale 3D-3D structures that confer advantages as electrode materials.Furthermore, incorporation of BC nanofibers in BC-PAN composites can regulate particle morphology and shape of derived carbon, thereby reducing grain boundary impedance and improving electrical conductivity.
Due to its easy processing and adjustable porosity, PMMA is also a typical polymer that can be used in the preparation of cellulose-derived carbon.Bai et al. utilized a combination of BC and PMMA to synthesize composites featuring a 3D inter-connected porous network through thermally induced phase separation [204].The schematic illustration of fabrication route of PMMA/BC composite Fig. 12 a Preparation of activated carbon monolith with microscale layer shape and nanoscale 3D-3D cross-linked structure, BC-PAN-AC [203]; b schematic illustration of fabrication route of PMMA/BC composite monolith and its conversion to functional activated carbon [204]; c schematic of the synthesis process of CNC/PEO-derived VCAs anodes; and d typical SEM images of a cross-sectional and top-view (inset) of the CNC/PEO aerogels.e EIS analysis of various cool rate [132]; and f rate performance of BC/PMMA derived carbon anode for SIBs [76].a Adapted with permission [203] Copyright 2018, Elsevier Limited.b Adapted with permission [204] Copyright 2018, Elsevier Limited.c-e Adapted with permission [132] Copyright 2022 Advanced Functional Materials published by Wiley-VCH GmbH.f Adapted with permission [76] Copyright 2022, the Royal Society of Chemistry 1 3 monolith and its conversion to functional activated carbon as show in Fig. 12b.Our group was devoting to modify cellulose precursors structure for improving electrochemical of SIBs.Taking advantage of the abundant micro/mesopores that PMMA pyrolysis formed, the optimized carbon anodes with a high specific surface area display an enhanced Na + diffusion rate with a high capacity of 380.66 mAh g −1 at a current density of 0.03 A g −1 [76].What' more, the stable network structure of BC-based carbon gives continuing conductivity pathway for electron, and display a better rate capacity as can be seen in Fig. 12f.
The microstructure of cellulose carbon materials with a directional charge transfer channel exhibits enhanced rate performance compared to the randomly oriented charge transfer pathway mentioned above.In Wang's work, a controllable unidirectional ice templating method (Fig. 12c was used to prepare cellulose nanocrystalline (CNC/polyethylene oxide (PEO) composites, and pyrolysis them to obtain vertically aligned carbon aerogels (VCAs) by controlling cool speed [132].From the cross-section (Fig. 12d and top-view SEMs) insert image of VCAs could see vertically aligned, channeled and honeycomb microstructure.Benefitted to the unique structure and oxygen groups introduced, VCAs-3 exhibits the lowest charge transfer resistance as shown in Fig. 12e.Mixed cellulose and polymer not only provide stable carbon conductive network, but hierarchically tailored and vertically aligned channels acting as ion reservoirs to boost electrolyte percolation.Based on the above, some polymers, as template or reinforcer, can tailor microstructure of cellulose precursor through changing their derived carbon nanodomains feature.Fabricating porous polymer monoliths, which plays a crucial role in tailoring the carbon porous structure, can be achieved through either polymerization or phase separation methods.However, this process is intricate and controlling the fine structure poses challenges [76,204].

Optimizing Valid Ion Transport Paths
Historically, decreasing thermodynamic energy barrier and increasing transport efficiency are the two most strategies for improving ion diffusion of anodes in SIBs.In order to decrease energy barrier, some studies stand on the view of defects and functional groups and link the simulation and theory calculated methods to analysis energy barriers change.Another way of ion diffusion to improve is constructing carbon microcrystalline and regulating porous structure.It cannot be overlooked is carbon microcrystalline particle and tortuosity ratio of electrode.Bigger microcrystalline particle is favorable to reversible capacity, but it leads to Na + diffusion limited due to a more quasi graphite sites will grow a bigger graphite domain.As well as tortuosity ratio, which is an essential factor to influence ion diffusion and electronic transfer [205].It is certain that lower tortuosity shows better transfer kinetic of ions.This section just discusses cellulose-based materials as carbon precursors to achieve fast ion diffusion and optimize the electrochemical performance of SIBs anode with the two strategies as above-mentioned.

Introducing Defects and Groups in Cellulose-Derived Carbon
The strategies of design defect carbon materials and function group are proposed to be efficient routes to achieve high Na + storage performance carbon-based materials.On the one hand, the presence of defects can enhance reaction kinetics due to the generation of a significant quantity of active sites.The introducing of defects on the electrode is advantageous for providing additional active sites and ion storage sites, thereby enhancing the insertion of metal ions and facilitating ion diffusion within the material.On the other hand, carboxylic anhydrides and quinone groups own two C=O bonds as a Na + reaction center, show stable configurations and good electronic conductivity, as well as strong Na + adsorption capability [206].In addition, oxygen functional groups can also improve the wettability of carbon anode toward electrolyte and thereby enhance the rate capability.Defects can be divided into two classes: intrinsic defect and non-intrinsic defect.The intrinsic defects in crystals of carbon materials include Schottky and Frenkel defects.Schottky defect occurs when atoms or ions leave vacancies in the lattice due to thermal vibration, while Frenkel defect happens when atoms or ions occupy interstitial sites.The electrochemical performance of carbonaceous materials is predominantly influenced by their local structures, particularly the pervasive intrinsic defects.The presence of intrinsic defects can lead to an enhanced capacitive process, and a distinct linear correlation has been observed between the (2024) 16: 148 148 Page 30 of 46 https://doi.org/10.1007/s40820-024-01351-2© The authors defects and electrochemical performance within a specific range [207,208].
Introducing defects can impact the intercalation and deintercalation of metal ions within the material layer by reducing stress and electrostatic repulsion between adjacent layers.This directly overcomes migration and diffusion barriers, promoting ion diffusion and charge transfer during the process of metal ion intercalation [181].It is well known that over-developed defects would break C-C sp 2 conjugated structure and therefore deteriorate the electric conductivity [209].C-C sp 3 defects enable efficient ion diffusion pathways.Moreover, defects can enhance the surface energy and facilitate electrochemical phase transitions.The strategy of constructing storage sites, which are defect sites, in electrode materials has gradually garnered researchers' attention due to their role as storage/adsorption/active sites for anchoring additional foreign ions or intermediate species during the reaction process to improve storage capacity [181].
The characterization of defects always used D band (disorder or defective structures) and G band (graphite structure of Raman spectra to illustration.The intensity ratio of D band and G band (I D /I G to analysis carbon structure disorder or defective degree.Yu and co-workers synthesized 3D interconnected with N/O-doped carbon (abbreviation NOC network composites, then through carbonized and active with KOH to obtain its derived carbon [210].Its Raman pattern exhibits higher I D /I G (1.12), and certifies that abundant defects and edge plane exposure exist in NOC.Due to higher specific surface area, the interface of electrode and electrolyte contact well and shortens the diffusion path for Na + (Fig. 13a).The disorder degree decreases with carbonization temperature increasing, therefore, introducing defects to improve ion diffusion speed need to suitably reduce temperature to carbonization.Sun et al. designed a new class of hard carbon material with controllable heteroatom doping and defects by an in-situ engineering approach, in which certain organic molecular vapor was mixed with Ar 2 carrier gas during the annealing process [211].Figure 13b illustrates the in-situ engineering process of hard carbon.In Fig. 13c, Na atom demonstrates a binding energy of + 0.45 eV on the pristine graphene sheet, while the adsorption energy for mono-defect, bi-defect, tri-defect, O doped and O&monodefect doped graphene are − 1.38, − 0.47, − 2.77, − 0.41, and − 3.32 eV, respectively, much lower than that of pristine graphene.Introducing defects into hard carbon would reduce adsorption energy and favorable to ion transfer and diffusion.
Recently, introduction of surface functional groups like oxygen-groups, on the carbon is a promising strategy to improve specific capacity by offering more ion adsorption sites to supply ion valid transport [212].Exception these advantages, a number of oxygen group on cellulose surface offer active sites for ions, and these ions with generated electronic form a well closed electronic circuit.The various functional groups in cellulose precursors directly influence the cross-linking process during heat treatment, which determine the defect microstructures of cellulose-derived carbon anode.Hu's group proposed that the rich oxygen groups and unsaturated bond are favorable to keep oxygen atoms cross-linking in the carbon precursors' structure to form C-O-C groups [213].To improve the structural diversity of cellulose-derived carbon materials for providing ion diffusion pathways, physical and chemical methods [214], polymer grafting [76], and functional group modification [215] has been used.
A simple mechanochemical strategy is used to introduce oxygen groups in the cellulose precursor [70].In Fig. 13d, the schematic of cellulose-derived carbon (shorted BHC-CO 2 ) prepared via dry ice-assisted ball milling method to introduce oxygen atoms, and certified by the distribution of different types oxygen-containing groups in C 1s pattern (Fig. 13e.It is obviously that BHC-CO 2 possesses the highest carboxyl group percentage of 8.38 at% (that is atomic percent), and exhibits good rate capacity of 293.5 and 122.3 mAh g −1 at current densities of 0.05 and 1 A g −1 (Fig. 13f.It is because that the surface-dominated Na + adsorption by selectively introducing carboxyl groups is enhanced.According to the interactions between Na and carboxyl-functionalized carbon surface in Fig. 13g, the adsorption energy of Na near carboxyl (− 214.7 kJ mol −1 ) is about 70 kJ mol −1 , higher than that on the pristine carbon surface (− 147.1 kJ mol −1 ), which indicates that the interaction of Na with carboxyl is much stronger than that with other oxygen-containing functional groups.The result ascribes to strong surface polarization and electron redistribution induced by the carboxyl functional group.

Improving the Crystalline Structure of Cellulose-Derived Carbon
The cellulose-derived carbon with a parallel hydrogen bond network exhibits exceptional crystallinity structure, which 1 3 is beneficial to enhance ions diffusion, electrical conductivity and reduce contact resistance between interfaces.The crystalline structure of cellulose-based carbon materials primarily encompasses the graphitization degree, the thickness (L c , length (L a ), interlayer distance (d 002 ) of graphite crystallite.The research on controlling interlayer distance is more focused than that on other crystalline parameters.According to the layer spacing, the microcrystalline structure of hard carbon can be classified into three types: highly disordered phases (d 002 > 0.4 nm), quasi-graphite phase (d 002 = 0.36-0.40nm), and graphite-like phase (d 002 < 0.36 [9]. High-temperature annealing is proved effective in facilitating atom rearrangement and enhancing graphitization degree, thereby augmenting the conductivity of carbon materials while allowing for tunable carbonaceous framework.Additionally, the graphitic domains of carbon materials may be influenced by the crystallinity of cellulose.The cellulose-derived carbon with lower crystallinity exhibits a highly disordered structure characterized by random chain orientation, which results in the higher rate capacity due to the adsorption of carrier ions on defects, edges, and micropores.Alvin et al. picked sulfur acid with various concentrations to treat microcrystalline cellulose powder, and its derived carbon as anode delivered a high reversible Fig. 13 a Transportation process of Na + and electron in the carbon network [210]; b the innovative in-situ engineering process for residual group control; and c atomic structure of Na + absorbed on pure graphene, and different defect graphene [211].d Fabrication process from HC to BHC-CO 2 and BHC-CO 2 -H 2 ; e distributions in C1s pattern of O-containing groups for HC, BHC-CO 2 , and BHC-CO 2 -H 2 ; f rate performances of HC, BHC-CO 2 , and BHC-CO 2 -H 2 anodes at various current densities; and g adsorption energy of adsorption energy of Na on the pristine carbon surface and near ether, ketone, hydroxyl, as well as carboxyl [70].a adapted with permission [210],  [216].Wang and his colleagues prepared highly dense conductive ramie carbon using a capillary evaporation strategy [217], as illustrated in Fig. 14a.The TEM images in Fig. 14b vividly reveal highly graphitized microcrystals (hGMCs) and a randomly oriented pseudo-graphite structure, which can provide numerous storage sites for electrolyte ions, benefiting both electron transmission and ion diffusion.
Recently, it is reported that reducing carbon crystalline size could reduce the ion diffusion length, bring high packing density, and improve structural stability [66,219].The reason that is the design of nanostructure can address issues in conventional battery materials, such as poor transport properties, significant volume changes at the particle and electrode level, instability of the electrode-electrolyte interface, and structural damage [220].The precise control of parameters such as size, shape, and morphology associated with Na + transport can lead to varying rate performances, which are important factors among all kinetic processes.In this context, our primary focus lies on optimizing the ion transport properties of nanomaterials in order to enhance ionic and electronic conduction pathways for improving rate performance.Nanofibers could generate interconnected network for Na + -ion diffusion channels and its interconnected porosity allows fast access of ionic species to the electrode surfaces [29,63].Another shell-core structure carbon also used to study storage sodium performance, because the hollow structure is benefited to boost ion transfer kinetics [218].With the number of shells increasing, the interface quantity between carbon and electrolyte are increasing and particle inner pores volume are also increasing. Figure 14c shows the rate performance of carbon materials with different number of shells, the clearly specific capacity increasing and charge transfer impendence reducing suggest that the unique structure is more favorable to higher reversible capacity and fast sodium ion transportation kinetics.The density of carbon is an essential factor to influence ions diffusion rate.A thick electrode with lower density carbon leads to a larger volume, but its active mass utilization is limited due to the longer ion diffusion pathway, which hinders volumetric capacitance [221].
Expanding the carbon interlayer distance (d 002 ) is usually used to improve ion transfer, the suitable distance of Na + insertion/extraction is 0.36 nm.The enlarged lattice distance and large specific surface area lead to excellent Na + storage performance [222].Exception for d 002 , the L a and L c of graphite crystallite are two important factors to determine ions transportation.Yin et al. synthesized hard carbon with the crystalline feature of larger L a and d 002 , and smaller L c via a ZnO-assisted bulk etching strategy [84].Besides, the ion diffusion coefficient highest D Na+ of 10 -6.88 cm 2 s −1 at the slope region, which slightly drops to 10 -7.48 cm 2 s −1 at the plateau region.The hard carbon with large d 002 , moderate L a , and L c , as well as high micropore volume, present higher reversible capacity and plateau capacity, Fig. 14d, e.As shown in Fig. 14f model, density functional theory (DFT) calculations are carried out to further explain that the short graphitic layer structures are beneficial for the adsorption of Na + and have minimal effect on the diffusion of sodium amidst the carbon layers.In addition, the relationship of between cellulose-based carbon structure and storage sodium performance is the focus of our group.In our work, in term of slope and plateau capacity suffer from the crystalline structure change whose change due to H 2 SO 4 pretreatment cellulose precursors [82].The two parameters of surface area and d 002 did not create positive influence on slope and plateau capacity, and depended on other factors, like pore structure (pore size and pore volume.

Regulating Porous Structure of Cellulose-Derived Carbon
Porous carbon materials not only provide efficient ion transport channels and a large number of available storage sites, but also significantly reduce volume expansion and promote disorder degree.Consequently, constructing a porous structure for hard carbon materials is an intensive studying strategy to improve rate performance and plateau capacity.
To our knowledge, surface area, pore size distribution, and pore volume are typical parameters to describer properties of porous materials.Plateau region storage sodium capacity is related to nanopores (especially closed pores) [223].Pore size distribution and surface charge of hard carbon affect whether sodium ions enter into the hard carbon or remain on the hard carbon surface [166].According to the IPUAC Technical report, macropore refers to a pore diameter of above 50 nm, mesopore refers to a pore diameter between 2 and 50 nm, and micropore refers to a pore diameter of below 2 nm.Moreover, micropore is classified as super-micropore and ultra-micropore (pore diameter < 0.7 nm) [224].Based on the above-mentioned content, porous structure plays an essential role to accelerate rate capacity.The cellulose unique structural feature, ultrafine nanoscale 3D fibrous and entangled network structure, resulting in a higher specific surface area and increased porosity [120].However, the intrinsic spatial structure at the molecular level imposes limitations on the specific surface area and pore structure of cellulose.For example, Wang et al. synthesized hierarchical porous loose sponge-like hard carbon (NHC-7) with a highly disordered phase prepared at a low temperature of 700 °C [225].It mainly had a pore diameter of about 4 nm and mesopores at around 50 nm, with a specific surface area of 602.1 m 2 g −1 (Fig. 15a, b.Enhancing electrolyte and electrode contact area and shorting ion diffusion pathways can increase the availability of surface Na + -ions, which results from the NHC-7 mesopores structure.
In addition, the hierarchically porous structure enables the construction of continuous connecting channels that accelerate electrolyte transport, resulting in the rapid formation of a complete SEI film (as shown in Fig. 15c) and facilitates its reaction kinetics.The porous structure of nitrogen-rich layered porous carbon materials derived from cellulose can also be effectively changed by boron doping [131].The porous structure in the interconnecting internal network has thinner pore walls and shorter carbon microcrystal length, and the Another approach aims to enhance the efficient utilization of materials and optimize the rational distribution of space for optimizing the ion transport process.Qiu's work prepared hollow hard-soft carbon spheres (HSCSs) by integrated melting-induced impregnation and mesoporeconfined carbonization [200].Meanwhile, combining with surface area and micropore reducing of BET analysis results, HSCSs deliver a relatively higher rate capacity of 210 and 179 mAh g −1 at the current densities of 0.1 and 1 A g −1 .This good conclusion is as follows: the soft carbon can enter into the pores and defects of hard carbon substances to tailor pore structure, which achieves transformation from mesopore to micropore and closed pore with the help of high temperature.In addition, hollow cavity can act as an electrolyte reservoir to decrease the diffusion distance from the bulk electrolyte to the electrode surface.Wang and co-workers used the altered thermal transformation pathway of chemical activation followed by high-temperature carbonization is adopted to achieve the conversion of open nanopores and ordered carbon crystallite into closed pores surrounded by short-range carbon structures and their carbon-marked CAC-1300 [226].They discussed in details that pore structure (surface area and closed pore created an impact on ICE, slope capacity, and plateau capacity (Fig. 15d. Figure 15e Fig. 15 Pore structure: a pore size distribution and b N 2 adsorption/desorption isotherms of different hard carbon samples, and c schematic diagram of Na + diffusion path in NHC-7 during operation [225]; d the relationship of pore structure and ICE, slope capacity, and plateau capacity; e schematic illustration of the pore structure evolution during various thermal treatment processes; and f sodium-ion battery based on CAC-1300 anode and NVP cathode [226].g The relationship between the plateau capacity and the mass ratio of the filler/host, ACGC, LCGC, and HCGC are corresponding active carbon, lower surface area, and higher surface area after carbonization obtained carbon, and h the capacity-potential curve [227]; and i comparison of the A parameters from SAXS in the Porod equation with BET surface area against the amount of MP [134].a-c Adapted with permission [225] Copyright 2020, The Nonferrous Metals Society of China and Springer-Verlag GmbH Germany.d-f Adapted with permission [226] Copyright 2022 Wiley-VCH GmbH.g, h Adapted with permission [227] Copyright 2022, Springer Nature.i Adapted with permission [134] Copyright 2019, WILEY-VCH Verlag GmbH & Co. KGaA 1 3 describes the process for successfully obtained change from open pore and closed pore.With Na 3 V 2 (PO 4 ) 3 (NVP) as a cathode and CAC-1300 as an anode to assemble full-cell, it shows good rate performance of 170.7 mAh g −1 at 1 °C and energy density up to 231.2 Wh kg −1 , as is shown in Fig. 15f.
Excepted among micropore, mesopore, and closed pore transformation, ultra-micropore structure is benefitted from ion diffusion and boosting rate capacity.Ultra-micropores (< 0.5 nm) of hard carbon can function as ionic sieves to reduce the diffusion of solvated Na + but allow the entrance of naked Na + into the pores, which can reduce the interface contact between the electrolyte and the inner pores without losing the fast diffusion kinetics [227].A lower filler/host ratio corresponding to more ultra-micropores can ensure a larger plateau capacity from Fig. 15g of quantitative relationship.And the rated capacity keeps 346 and 125 mAh g −1 at 0.3 and 2 A g −1 .From Fig. 15h, one can know without peak change in XRD pattern during SIBs operation, which suggests no intercalation/deintercalation into/from the graphitic interlayers in both the sloping region and plateau region.Therefore, the existence of an ultra-micropore can provide a more active site for ion storage and expand ion diffusion accessibility.The previously mentioned combination of hard and soft carbon to tailor closed pore numbers by changing the mass ratio of hard and soft carbon [134].Small-angle X-ray scattering (SAXS) and N 2 adsorption methods are used to investigate the pore structure and surface area variation (Fig. 15i), which express that the soft carbon limits access to the pore surface resulting in a higher fraction of closed pores.Meanwhile, hard-soft carbon, as an anode for SIBs, shows excellent electrochemical performance, especially rate, due to soft carbon precursors blocking open pores of hard carbon and keeping a stable structure for ion diffusion.
The self-supporting carbon electrodes with advantageous porous structure for valid ion transportation have reported studies [72,89,195].Hu's group focused on the conversion of wood-based materials into carbon electrodes through carbonization.The resulting carbon exhibits a unique mesoporous structure with a high percentage of short-range ordered lattice and a large amount of carbon nanofibers [72].By controlling thickness of the cut wood, they were able to achieve various thicknesses for the free-standing carbon electrode [205].The development of free-standing electrodes has promoted research on thick electrodes.In addition to wood, bacterial cellulose has been studied by direct carbonization to prepare self-supporting materials [89].Under the carbonization condition of 1300 °C, the resulting carbon films exhibit excellent rate capability, with values of 147 and 128 mAh g −1 at 10 and 20 A g −1 , respectively.The limited applications of the flexible electrode are due to its inability to load sufficient mass of active materials.Guo et al. developed a self-supporting electrode (NVP@C-CC using carbon cloth (CC as a support material for loading high mass Na 3 V 2 (PO 4 ) 3 @carbon (NVP@C [228].The NVP@C-CC exhibits a higher rate capacity of 96.8 mAh g −1 at 100 °C and 69.9 mAh g −1 at 200 °C, while also providing the cell with high energy and power densities of 396 Wh kg −1 and 97 kW kg −1 .
There are some questions for influence on ions diffusion of pore structure.Whether closed pore or open pore?micropore or mesopore?Which of them is more favorable to sodium ion diffusion?More and more attentions have been paid to the fact that closed pore make real effect on storage sodium ion behaviors.For an example, with temperature increasing, waste cork-derived hard porous carbon with rich closed pore is transformed open pore [117].Zhao et al. synthesized carbon materials via altering thermal transformation pathway of chemical activation followed by high-temperature carbonization [226].Carbon with micro/ mesoporous could offer more contacts between the sodium ions and the host materials, shortening the ion transport path lengths and accelerating the electrochemical reactions [113,229].Compared with open pores, in which de-solvated Na + ions enter through these openings, diffuse and gather inside the pore, the storage sodium behaviors of closed pore structures are tended to near metallic sodium deposition.

Summary and Perspectives
Raising the fast-charging capability of sodium ions batteries is a key requirement for the adoption of current batterybased electric vehicles and consumer electronics.However, current sodium-ion batteries are still unable to support ultrafast power input due to the larger ionic radium, resulting the capacity fade at high current densities, that is also a key technological barrier for hard carbon anodes.In this review, we systematically summarize the structural characteristics of cellulose materials and cellulose-derived carbon materials.Taking into account the intrinsic structural limitation of cellulose materials, we discuss two strategies for enhancing (2024) 16: 148 148 Page 36 of 46 https://doi.org/10.1007/s40820-024-01351-2© The authors the rate-capability of cellulose-derived carbon materials from the perspective of ion diffusion and charge transfer.Specific methods include but not limited to, constructing an interconnected transportation network, regulating molecular structure of cellulose precursors, increasing the graphitization degree, and tailoring crystalline structures of cellulosederived carbons.Despite a series of cellulose-derived hard carbon have been applied in sodium ions batteries, there are some key points that need to be addressed on developing high-rate performance of anode materials.

(i) Increasing the Purity of Cellulose-Based Materials
It is well-known that a large amount of composition such as cellulose, hemicellulose, lignin, starch, and ash exist in natural cellulose-based materials.When cellulose-based materials are carbonized at high temperature, the structure of cellulose-derived carbon is determined through the interaction of these components.Among these components, a few of impurities have negative effect on the electronic conductivity of cellulose-derived carbons, thus affecting the rate performance of SIBs.Since residual impurities in chemical components can negatively affect the performance and also lead to a serious increase in side reaction, it is highly desirable to develop a suitable purification process to decrease the amounts of impurities in cellulose-based precursors.(ii) Optimizing the Crystalline Structure at Molecular Level A large number of hydroxyl groups exist on the cellulose chain that can form internally strong hydrogen bonds, which make other active groups or molecular hard to access.The most commonly employed chemical modification of involves substituting the alcoholic hydroxyl group at the C6 position in cellulose chains, which preserves precursors' inherent morphology and a high carbon yield.At present, the mechanism on thermochemical changes and the microstructure of hard carbon during cellulose materials pyrolysis remains unclear, while further investigation is required to determine how the reactivity of other alcohol hydroxyl groups (such as C 2 -OH affects porous structure.The systematic research will help to accurately predict the properties of carbon materials upon formation.Therefore, molecule-level functionalization or modification is beneficial to optimize the crystalline of cellulose-based materials, enabling regulate graphite and disorder structure of cellulosederived carbon materials. (iii) Valuing Pre-treatment Process Before High-Temperature Pyrolysis Due to their varying compositions, irregular porous structure, and complex carbonization, cellulose-based precursors have an uncontrolled crystalline structure.Besides, the pyrolysis behavior of cellulose-based materials is influenced by variations in chemical molecular, functional groups, and aggregation states of precursors.Therefore, pretreatment strategies are necessary to optimize the structure of cellulose-derived hard carbon for sodium ion batteries.It includes not only purification component of precursors using chemical/physical methods, but also pre-carbonized process aiming at intermediate carbon products.Through pre-treatment process, cellulose-derived carbon materials show a higher plateau and slope capacity, exhibiting a better rate performance.(iv) Regulating Carbon Edge Structure and Pore Engineering Advanced cellulose-derived anodes with high-rate performance range by employing appropriate carbon edge structure and pore engineering are critical, since the both dictates the ion transport and interfaces for a given battery chemistry.Carbon structures with reduced open pores, abundant closed pores, and appropriate carbon interlayer spacing present a formidable challenge.High-temperature treatment can effectively decrease the specific surface area of cellulose-derived carbons and convert their open pores into closed ones, enhancing plateau capacity and initial coulombic efficiency.Nevertheless, significantly decreased interlayer spacing caused by high-temperature treatment may hinder the transport of sodium ions.Therefore, these critical parameters should be carefully balanced through optimizing precursors or pyrolysis processes to explore the relationship between carbon microstructure and performance in different electrolytes for designing promising carbon materials for SIBs.
Huge advances in designing cellulose-derived anode materials with excellent rate performances have been achieved, however, there are many challenges to further improve rate performances, especially how to better combine each strategy and balance their advantage and shortcomings.We believe that the guidelines presented will provide an avenue for designing high-rate anodes for next-generation sodium-ion batteries.

Fig. 1 a
Fig. 1 a The supra-molecular structure and aggregation structure of cellulose (the primary three conformations of hydroxyl group in the insert Fig.); b conversion between homogeneous polycrystalline of cellulose (the abbreviation of EDA, GLY and AML refer to ethanediamine, glycerinum and liquid ammonia; and c the reaction active groups of cellulose molecular chains

Fig. 6
Fig. 6 The relationship of sodium storage and rate performance for cellulose-based carbon in our previous work: a GCD curves; b rate capacity at different current densities [82]; c the fitted curves of capacity versus rate data with semi-empirical equation for batteries electrodes; d CV curves at different sweeps; e capacity ratios at sweep speed 0.1 mV s −1 ; f the b value & peak current under different sweep rates [76]; g capacity ratios at different sweep rates; and h the comparing rate capacity in the different cellulose-derived hard carbon materials.a, b Adapted with permission[82], Copyright 2022, Elsevier Limited.d-f Adapted with permission [76], Copyright 2022, the Royal Society of Chemistry /doi.org/10.1007/s40820-024-01351-2© The authors /doi.org/10.1007/s40820-024-01351-2© The authors Fig.8The strategies of improving rate capacity of cellulose-derived carbon materials at cellulose materials level.Optimizing valid ion transport paths strategies on the above line are doping in cellulose precursors[178,179], combining in cellulose precursors[180], and polymerizing in cellulose precursors[76]; building robust charge transport network strategies on the below line are introducing defects and groups[181], improving the crystalline structure[73,89], and regulating porous structure[182].Doping: Adapted with permission[178,179], Copyright 2020, Elsevier B.V. and Copyright 2021, Royal Society of Chemistry.Combing: Adapted with permission [180].Copyright 2012, American Chemical Society.Polymering: Adapted with permission [76], Copyright 2022, the Royal Society of Chemistry.Defects/groups: Adapted with permission [181], Copyright 2020, WILEY-VCH Verlag GmbH & Co. KGaA.Porous structure: Adapted with permission [182], Copyright 2022, Elsevier Limited.Crystalline structure: Adapted with permissioned [73, 89], Copyright 2022, Wiley-VCH GmbH and Copyright 2019, Elsevier B.V

Fig. 9 N
Fig. 9 N-doping [185]: a fabrication of N-doping composite electrode; b EIS spectra of N-doping electrodes at charging state after cycles and the inset images of equivalent circuits; and c illustration of N-doping carbon with different doping sites.N/S co-doping [66]: d the sodium storage behavior occurring in the N/S-doped carbon; and e graphical illustration of the carbon structures in common graphite, undoped hard carbon, and N/S co-doped hard carbon with different interlayer distances and their influences on the Na-storage capabilities.N-doping: a-c Adapted with permission [185], Copyright 2018, Elsevier B.V. N/S co-doping: d, e adapted with permission [66],Copyright 2016, WILEY-VCH Verlag GmbH & Co. KGaA, Weinheim

Fig. 11 a
Fig. 11 a Schematic reduction and microwaving of GO-CNF; b rate performance of MrGO-CNF at various current density [135]; c schematic illustration of the prepared porous Co 3 O 4 @N-CNFs composite; d SEM image of the Co 3 O 4 @N-CNFs [184]; e rate performance and capacity retention rates of various carbons; f the contribution ratios of slope capacity and plateau capacity; and g FTIR spectra of commercial paper towels and coal pitch [195].a, b Adapted with permission [135], Copyright 2019, WILEY-VCH Verlag GmbH & Co. KGaA.c-d Adapted with permission [184], Copyright 2020, Elsevier B.V. e-g Adapted with permission [195], Copyright 2021, American Chemical Society Fig.13a Transportation process of Na + and electron in the carbon network[210]; b the innovative in-situ engineering process for residual group control; and c atomic structure of Na + absorbed on pure graphene, and different defect graphene[211].d Fabrication process from HC to BHC-CO 2 and BHC-CO 2 -H 2 ; e distributions in C1s pattern of O-containing groups for HC, BHC-CO 2 , and BHC-CO 2 -H 2 ; f rate performances of HC, BHC-CO 2 , and BHC-CO 2 -H 2 anodes at various current densities; and g adsorption energy of adsorption energy of Na on the pristine carbon surface and near ether, ketone, hydroxyl, as well as carboxyl[70].a adapted with permission[210], Copyright 2016, WILEY-VCH Verlag GmbH & Co. KGaA; b, c adapted with permission [211], Copyright 2019, Published by Elsevier Limited.d-g Adapted with permission [70], Copyright 2019 American Chemical Society

Fig. 14 a
Fig. 14 a Strategy of preparing high-dense conductive ramie carbon (hd-CRC by pyrolysis after chemical stripping and capillary evaporation on dense cellulose molecules, b TEM image of hd-CRC revealing the highly graphitized microcrystals (hGMCs) [217]; c The rate performance for four carbon samples with different shell number [218]; d Comparison of d 002 , I D /I G , and e L a and L c of different samples; f Model of short graphitic layer and nanopore about DFT calculation [84]; the correction of g the specific surface area and slope capacity, h the values of d 002 and plateau capacity [82].a, b Adapted with permission [217].Copyright 2023, Wiley-VCH GmbH.c Adapted with permission [218].Copyright 2018, WILEY-VCH Verlag GmbH & Co. KGaA, d-f Adapted with permission [84], Copyright 2022, Wiley-VCH GmbH.g, h Adapted with permission [82] Copyright 2022, Elsevier Limited /doi.org/10.1007/s40820-024-01351-2© The authors positive effect of ion diffusion is faster under the weakened diffusion barrier, thus shortening the diffusion time.

Table 1
The proportion of cellulose in different raw materials

Table 2
Lattice parameters of the most common cellulose allomorphs

Table 3
Comparison of diffusion coefficients, capacity, and ion diffusion lengths of different cellulose-derived carbon materials